Influência da adição de sal de ônio na diminuição do amarelamento e nas propriedades de cimentos resinosos experimentais [recurso eletrônico] = Effect of diphenyliodonium hexafluorphosphate in the reduction of yellowing and on the properties of experimental resin cements
Kamila Menezes Guedes de Andrade
TESE
T/UNICAMP An24i
[Effect of diphenyliodonium hexafluorphosphate in the reduction of yellowing and on the properties of experimental resin cements]
Piracicaba, SP : [s.n.], 2016.
1 recurso online (47 p.) : il., digital, arquivo PDF.
Orientador: Giselle Maria Marchi Baron
Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba
Resumo: O objetivo deste estudo foi avaliar o efeito da adição do sal Hexafluorofosfato de Difeniliodônio (DPI) nas propriedades de cimentos resinosos experimentais fotopolimerizáveis e sua influência na análise de cor. À composição base (1:1 em peso) de monômeros Bisfenol A Diglicidil Metacrilato...
Ver mais
Resumo: O objetivo deste estudo foi avaliar o efeito da adição do sal Hexafluorofosfato de Difeniliodônio (DPI) nas propriedades de cimentos resinosos experimentais fotopolimerizáveis e sua influência na análise de cor. À composição base (1:1 em peso) de monômeros Bisfenol A Diglicidil Metacrilato (BisGMA) e Trietilenoglicol Dimetacrilato (TEGDMA) foi adicionado 0,1 mol% do inibidor Hidroxitolueno Butilado (BHT). Canforoquinona (CQ) e Dimetilaminoetil Benzoato (EDAB) foram adicionados em 2 diferentes concentrações com ou sem a adição de 0,5 mol% DFI, resultando em oito grupos experimentais: RC1 (0,5 mol% CQ/1mol% EDAB sem sal), RC2 (0,5 mol% CQ/ 2mol% EDAB sem sal), RC3 (1mol%CQ/1mol%EDAB sem sal), RC4 (1mol%CQ/2mol%EDAB sem sal), RC5 (0,5 mol% CQ/1mol% EDAB com sal), RC6 (0,5 mol% CQ/ 2mol% EDAB com sal), RC7 (1mol%CQ/1mol%EDAB com sal), RC8 (1mol%CQ/2mol%EDAB com sal). Após a manipulação da matriz resinosa, 60% em peso de partículas inorgânicas silanizadas de vidro de bário-alumínio-silicato foram adicionadas. As propriedades analisadas foram grau de conversão (DC) (n=5) pelo espectrômetro de raios infra-vermelhos transformado de Fourier, análise de cor (Y) (n=10) através da leitura por espectrofotômetro pelo sistema CIELab, sorção (WS) e solubilidade (S) em água destilada (n=5), Resistência à flexão (FS) e módulo de elasticidade (E) (n=10). A análise estatística foi realizada com significância de 5%, para cada teste separadamente, pelo ANOVA três fatores e teste de Tukey. O teste Mann Whitney foi utilizado para variável L* na análise de cor. Os resultados mostraram que a adição do DFI aumentou o grau de conversão e L*, sem aumentar sorção e valores de a* b* em cimentos contendo 0,5mol%CQ. Quanto mais CQ, maiores valores de b* e menores valores de sorção sem o sal. Os grupos com EDAB 2mol% apresentaram maior DC. Pode-se concluir que a adição de DFI permite a diminuição da CQ com efeito de menor amarelamento, mantendo propriedades adequadas nos cimentos experimentais testados
Ver menos
Abstract: The aim of this study was to evaluate the effect of the addition of the Diphenyliodonium Hexafluorophosphate (DPI) on the properties of experimental light-cured resin cements and its influence on the color analysis. To the monomers base composition (1:1 mass ratio) Bisphenol A Diglycidyl...
Ver mais
Abstract: The aim of this study was to evaluate the effect of the addition of the Diphenyliodonium Hexafluorophosphate (DPI) on the properties of experimental light-cured resin cements and its influence on the color analysis. To the monomers base composition (1:1 mass ratio) Bisphenol A Diglycidyl Methacrylate (BisGMA) and Triethylene Glycol Dimethacrylate (TEGDMA) 0.1mol% Butylated Hydroxytoluene (BHT) was added as an inhibior. Camphorquinone (CQ) and Dimethylamino Ethyl Benzoate (EDAB) were added at 2 different concentrations with or without the addition of 0.5mol% DPI, resulting in eight groups: RC1 (0.5mol% CQ / EDAB1mol% without salt) , RC2 (0.5mol% CQ / 2mol% EDAB without salt), RC3 (1mol% CQ / 1mol% EDAB without salt), RC4 (1mol% CQ / 2mol% EDAB without salt), RC5 (0.5mol% CQ / 1mol% EDAB with salt), RC6 (0.5mol% CQ / 2mol% EDAB with salt), RC7 (1mol% CQ / 1mol% EDAB with salt), RC8 (1mol% CQ / 2mol% EDAB with salt). After the manipulation of the resinous matrix, 60wt% of silanated barium-aluminum-silicate glass was added as a filler. The studied properties were the following: Degree of Conversion (DC) (n=5) by Fourier transformed infrared spectrometer; L*a*b* Color Analysis (Y) by reflectance spectrophotometer with CIELab system; Sorption (WS) and Solubility (S) in distilled water (n=5); Flexural Strength (FS) and Young's Modulus (E) (n=10). Statistical analysis (?=0.05) was performed for each test separately by ANOVA three way and Tukey¿s test. Shapiro Wilk and Mann Whitney were used for color analysis (L* variable). The results showed that the addition of the DPI increased the degree of conversion and L* without increasing the sorption and the values of a*b* in cements containing 0.5mol% CQ. The more CQ, the higher the b* values and the lower sorption without salt are. Groups with EDAB 2mol% showed a higher DC. It can be concluded that the addition of the DPI allows the reduction of the CQ with a lower yellowing effect, maintaining adequate properties in the experimental cements tested
Ver menos
Requisitos do sistema: Software para leitura de arquivo em PDF
Marchi, Giselle Maria, 1970-
Orientador
Martins, Luís Roberto Marcondes, 1960-
Avaliador
Aguiar, Flavio Henrique Baggio, 1977-
Avaliador
Mitsui, Fabio Hiroyuki Ogata
Avaliador
Matuda, Larissa Sgarbosa de Araújo
Avaliador
Influência da adição de sal de ônio na diminuição do amarelamento e nas propriedades de cimentos resinosos experimentais [recurso eletrônico] = Effect of diphenyliodonium hexafluorphosphate in the reduction of yellowing and on the properties of experimental resin cements
Kamila Menezes Guedes de Andrade
Influência da adição de sal de ônio na diminuição do amarelamento e nas propriedades de cimentos resinosos experimentais [recurso eletrônico] = Effect of diphenyliodonium hexafluorphosphate in the reduction of yellowing and on the properties of experimental resin cements
Kamila Menezes Guedes de Andrade