Síntese de nanocompósitos poliméricos de poli(acrilato de n-butila-co-metacrilato de metila) P(BA-co-MMA) e Hidróxidos Duplos Lamelares (HDL) por meio da técnica de polimerização em miniemulsão
DISSERTAÇÃO
Português
T/UNICAMP Si38s
[Synthesis of polymeric nanocomposites of poly(n-butyl acrylate-co-methyl methacrylate) P(BA-co-MMA) and Layered Double Hydroxides (LDH) through miniemulsion polymerization]
Campinas, SP : [s.n.], 2011.
71 f. : il.
Orientador: Liliane Maria Ferrareso Lona
Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química
Resumo: O objetivo deste trabalho foi sintetizar nanocompósitos poliméricos (NCPs) contendo Hidróxidos Duplos Lamelares (HDLs) por meio da técnica de polimerização em miniemulsão. O copolímero poli(acrilato de n-butila-co-metacrilato de metila) P(BA-co- MMA) foi escolhido como matriz dos NCPs devido...
Resumo: O objetivo deste trabalho foi sintetizar nanocompósitos poliméricos (NCPs) contendo Hidróxidos Duplos Lamelares (HDLs) por meio da técnica de polimerização em miniemulsão. O copolímero poli(acrilato de n-butila-co-metacrilato de metila) P(BA-co- MMA) foi escolhido como matriz dos NCPs devido à sua importância comercial na formulação de adesivos sensíveis à pressão (PSA). Os HDLs organicamente modificados disponíveis comercialmente Perkalite F100S, Perkalite A100 e Perkalite AF50 foram usados como agentes de reforço dos nanocompósitos. A metodologia utilizada foi semelhante a metodologia utilizada para produção de NCPs contendo argilas catiônicas pela polimerização em miniemulsão, na qual a carga mineral é adicionada à fase orgânica antes da produção das miniemulsões. Os látices obtidos foram caracterizados por: Difração de Raios-X (DRX), Espalhamento Dinâmico de Luz (DLS), Calorimetria Exploratória Diferencial (DSC), Análise Termogravimétrica (TG) e Microscopia Eletrônica de Transmissão (MET)
Abstract: The aim of this work was the synthesis of polymeric nanocomposites (PNCs) filled with Layered Double Hydroxides (LDHs) through miniemulsion polymerization. The copolymer poli(n-butyl acrylate-co-methyl methacrylate) P(BA-co-MMA) was chosen to form the matrix because it is a commercially...
Abstract: The aim of this work was the synthesis of polymeric nanocomposites (PNCs) filled with Layered Double Hydroxides (LDHs) through miniemulsion polymerization. The copolymer poli(n-butyl acrylate-co-methyl methacrylate) P(BA-co-MMA) was chosen to form the matrix because it is a commercially important component in the formulation of pressure sensitive adhesives (PSA). The commercial available organically modified LDHs Perkalite F100S, Perkalite A100 and Perkalite AF50 were used as fillers. The methodology used was similar to the one used to produce PNCs filled with cationic clays through miniemulsion polymerization, where the inorganic charge is added to the organic phase before the preparation of the miniemulsion. The latexes prepared were characterized by: X-Ray Diffraction (XDR), Dynamic Light Scattering (DLS), Differential Scanning Calorimetry (DSC), Thermogravimetric Analysis (TG) and Transmission Electron Microscopy (TEM)
Síntese de nanocompósitos poliméricos de poli(acrilato de n-butila-co-metacrilato de metila) P(BA-co-MMA) e Hidróxidos Duplos Lamelares (HDL) por meio da técnica de polimerização em miniemulsão
Síntese de nanocompósitos poliméricos de poli(acrilato de n-butila-co-metacrilato de metila) P(BA-co-MMA) e Hidróxidos Duplos Lamelares (HDL) por meio da técnica de polimerização em miniemulsão
Exemplares
Nº de exemplares: 2
Não existem reservas para esta obra