Comparação das propriedades mecânicas e superficiais das resinas para placa oclusal manufaturadas por tecnologia aditiva ou subtrativa [recurso eletrônico]
André Barros de Held
TESE
Português
T/UNICAMP H366c
[Comparassion of the mechanical properties of occlusal splint resins manufactured by additive or subtractive technology]
Piracicaba, SP : [s.n.], 2023.
1 recurso online (43 p.) : il., digital, arquivo PDF.
Orientador: Wander José da Silva
Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba
Resumo: As placas oclusais CAD-CAM fabricadas com tecnologia aditiva têm apresentado vantagens crescentes em relação à tecnologia subtrativa, com menor custo, menor produção de resíduos e maior produtividade. No entanto, há um conhecimento limitado sobre as propriedades dessas resinas para...
Ver mais
Resumo: As placas oclusais CAD-CAM fabricadas com tecnologia aditiva têm apresentado vantagens crescentes em relação à tecnologia subtrativa, com menor custo, menor produção de resíduos e maior produtividade. No entanto, há um conhecimento limitado sobre as propriedades dessas resinas para fundamentar cientificamente se a impressão 3D pode substituir a fresagem. O objetivo deste estudo foi comparar as propriedades mecânicas e superficiais de resinas acrílicas utilizadas para impressão ou fresagem de placas oclusais. Um total de 30 espécimes retangulares e 30 discos de resina acrílica foram preparados por meio de fresagem (F) ou impressão (I) (n=15). O teste de resistência à flexão foi realizado com uma máquina Instron, de acordo com a norma ISO 4049:2019 e o módulo de elasticidade foi calculado. O teste de microdureza Knoop utilizou um microdurômetro; o teste de rugosidade superficial foi realizado por meio de um perfilômetro; e a energia livre superficial e a molhabilidade foram medidas por meio de um goniômetro. As características topográficas foram observadas por meio de microscópio eletrônico de varredura. Os dados foram analisados com o teste-t independente, a 5% de significância. As resinas fresadas apresentaram menor resistência à flexão (F = 71,12 ± 15,12; I = 82,76 ± 6,51 MPa), e maior microdureza (F = 22,08 ± 2,32; I = 14,40 ± 6,41 KHN) e módulo de elasticidade (F = 2,83 ± 0,15; I = 2,17 ± 0,17 GPa) do que as impressas. A energia livre superficial e a molhabilidade das resinas fresadas foram menores, com menor componente dispersivo do que as impressas. Os valores de rugosidade foram semelhantes (P>0,05). A análise topográfica revelou que as superfícies impressas tinham camadas que se desprenderam, enquanto os espécimes fresados estavam mais homogêneos. Concluiu-se que a resina impressa apresentou características mecânicas e superficiais inferiores às fresadas, com exceção da resistência à flexão e rugosidade. Ambas resinas precisam de aprimoramento em suas propriedades para serem utilizadas na fabricação de placas oclusais
Ver menos
Abstract: Additive-manufactured CAD-CAM occlusal splints have presented increasing fabrication advantages over subtractive-manufactured ones, with lower cost, less waste production, and increased productivity. However, there is limited knowledge about the mechanical properties of these resins to...
Ver mais
Abstract: Additive-manufactured CAD-CAM occlusal splints have presented increasing fabrication advantages over subtractive-manufactured ones, with lower cost, less waste production, and increased productivity. However, there is limited knowledge about the mechanical properties of these resins to scientifically ground whether 3D printing can replace milling. The purpose of this study was to compare mechanical and superficial properties of the acrylic resins used for printing or milling occlusal splints. A total of 30 retangular and 30 disk-shaped specimens were prepared with milled (M) or printed (P) acrylic resins (n = 15). The flexural resistance test was performed using an Instron machine, according to ISO 4049:2019 and the elasticity modulus was calculated. The Knoop microhardness test was performed using a microhardness test device; the surface roughness test was performed by using a profilometer, and the surface free energy and wettability were measured using a goniometer. The topographic characteristics of the specimens were observed by means of a scanning electron microscope. Data were analyzed using an independent sample t-test at 5% significant level. The milled resins had lower flexural strength (M = 71.12 ± 15.12; P = 82.76 ± 6.51 MPa) and higher microhardness (M = 22.08 ± 2.32; P = 14.40 ± 6.41 KHN) and modulus of elasticity (F = 2.83 ± 0.15; I = 2.17 ± 0.17 GPa) than the printed ones. The surface free energy and wettability of the milled resins were lower, with lower dispersive component than the printed ones. Roughness values were similar (P > 0.05). Topographic analysis revealed that the printed surfaces had microlayers that detached from the specimen during the polishing procedures while milled specimens were more homogeneous. In this study, the following conclusions were drawn: the printed resin showed lower mechanical and superficial characteristics than the milled resins, except for the flexural strength and roughness. Both resins need improvements in their mechanical and surface properties for use in the manufacture of occlusal splints
Ver menos
Silva, Wander José da, 1980-
Orientador
Campos, Francisco Ubiratan Ferreira de
Avaliador
Montagner, Antonio Marcos, 1971-
Avaliador
Consani, Rafael Leonardo Xediek, 1974-
Avaliador
Ricomini Filho, Antônio Pedro, 1983-
Avaliador
Comparação das propriedades mecânicas e superficiais das resinas para placa oclusal manufaturadas por tecnologia aditiva ou subtrativa [recurso eletrônico]
André Barros de Held
Comparação das propriedades mecânicas e superficiais das resinas para placa oclusal manufaturadas por tecnologia aditiva ou subtrativa [recurso eletrônico]
André Barros de Held