Avaliação in vivo da migração local de íons bismuto e silício presentes em cimentos reparadores em contato com tecido conjuntivo e ósseo [recurso eletrônico]
Tamires Melo Francati
DISSERTAÇÃO
Português
T/UNICAMP F844a
[In vivo evaluation of the local migration of bismuth and silicon ions present in repair cements in contact with connective tissue and bone]
Piracicaba, SP : [s.n.], 2022.
1 recurso online (61 p.) : il., digital, arquivo PDF.
Orientador: Marina Angélica Marciano da Silva
Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba
Resumo: O agregado trióxido mineral (MTA) é um cimento utilizado na endodontia em procedimentos reparadores, composto por silicato tricálcio, silicato dicálcio, aluminato tricálcio e o radiopacificador óxido de bismuto. O objetivo deste estudo é avaliar a migração e o acúmulo local de íons bismuto...
Ver mais
Resumo: O agregado trióxido mineral (MTA) é um cimento utilizado na endodontia em procedimentos reparadores, composto por silicato tricálcio, silicato dicálcio, aluminato tricálcio e o radiopacificador óxido de bismuto. O objetivo deste estudo é avaliar a migração e o acúmulo local de íons bismuto (Bi) após contato com tecido conjuntivo e ósseo. O estudo avaliou também a hipótese de que o mecanismo de migração do bismuto está associado ao silício (Si). Um total de 64 ratos Wistar foram divididos em grupos experimentais de acordo com o tecido de implantação: conjuntivo e ósseo, e com os cimentos implantados: silicato tricálcio (TCS) (n=20), ProRoot MTA (MTA) (n=20), hidroxiapatita com 20% de óxido de bismuto (HAp-Bi) (n=20), e controle negativo, sem implantação (n=4). Os animais foram sacrificados após 30 (n=32) e 180 dias (n=32). As metodologias utilizadas para avaliação da migração do Bi e Si, em ambos os tecidos, foram espectrometria de fluorescência de raios-X (XRF), espectrometria de massa de plasma indutivamente acoplado (ICP-MS), caracterização química por meio de espectroscopia Raman e análise histológica da resposta tecidual. A análise estatística dos resultados da avaliação multielementar em ICP-MS e da avaliação histológica, foi realizada considerando o nível de significância de 5% (p < 0,05). A análise XRF demonstrou a migração do Bi do MTA e HAp-Bi em direção ao tecido conjuntivo e ósseo, sugerindo que esta migração ocorre independente do Si, pois o grupo HAp-Bi não apresenta este elemento. Na análise em ICP-MS, para o grupo MTA e Hap-Bi foi possível detectar o bismuto nos tecidos conjuntivo e ósseo em ambos os períodos. Para o tecido conjuntivo, não houve diferença estatística entre os grupos MTA e Hap-Bi, para o bismuto (p > 0,05). O elemento silício foi detectado em todos os grupos, com maior fração de massa no tecido conjuntivo após 30 dias para os grupos TCS e MTA, porém sem diferença estatística entre eles (p > 0,05). A análise Raman mostrou pequenos sinais de alterações para todos os materiais implantados aos 180 dias, independentemente do local de implantação. Histologicamente, foi observada uma elevada inflamação aos 30 dias para todos os grupos experimentais, em ambos os tecidos. Porém aos 180 dias no tecido ósseo, esta inflamação reduziu significativamente (p < 0,05). O contato do cimento ProRoot MTA com os tecidos conjuntivo e ósseo resulta na migração do bismuto. Entretanto, o mecanismo de migração deste elemento sugere que pode ocorrer de forma independente do silício
Ver menos
Abstract: Mineral trioxide aggregate (MTA) is a cement used in endodontics in reparative procedures, composed of tricalcium silicate, dicalcium silicate, tricalcium aluminate and the radiopacifier bismuth oxide. The aim of this study is to evaluate the migration and local accumulation of bismuth...
Ver mais
Abstract: Mineral trioxide aggregate (MTA) is a cement used in endodontics in reparative procedures, composed of tricalcium silicate, dicalcium silicate, tricalcium aluminate and the radiopacifier bismuth oxide. The aim of this study is to evaluate the migration and local accumulation of bismuth (Bi) ions after contact with connective tissue and bone. The study also evaluated the hypothesis that the bismuth migration mechanism is associated with silicon (Si). A total of 64 Wistar rats were divided into experimental groups according to the implantation site: connective and bone, and with the implanted cements: tricalcium silicate (TCS) (n=20), ProRoot MTA (MTA) (n=20) , hydroxyapatite with 20% bismuth oxide (HAp-Bi) (n=20), and negative control, without implantation (n=4). The animals were sacrificed after 30 (n=32) and 180 days (n=32). The methodologies used to evaluate the migration of Bi and Si in both tissues were X-ray fluorescence spectrometry (XRF), inductively coupled plasma mass spectrometry (ICP-MS), chemical characterization by means of Raman spectroscopy and histological analysis of tissue response. Statistical analysis of the results of the multi-element evaluation in ICP-MS and of the histological evaluation was performed considering a significance level of 5% (p < 0.05). XRF analysis demonstrated the migration of Bi from MTA and HAp-Bi towards connective tissue and bone, suggesting that this migration occurs independently of Si, as the HAp-Bi group does not present this element. In the ICP-MS analysis, for the MTA and Hap-Bi group, it was possible to detect bismuth in the connective and bone tissues in both periods. For connective tissue, there was no statistical difference between the MTA and Hap-Bi groups for bismuth (p > 0.05). The silicon element was detected in all groups, with a higher mass fraction in the connective tissue after 30 days for the TCS and MTA groups, but with no statistical difference between them (p > 0.05). Raman analysis showed small signs of change for all implanted materials at 180 days, regardless of implantation site. Histologically, elevated inflammation was observed at 30 days for all experimental groups, in both tissues. However, at 180 days in bone tissue, this inflammation significantly reduced (p < 0.05). Contact of ProRoot MTA cement with connective and bone tissue results in bismuth migration. However, the migration mechanism of this element suggests that it can occur independently of silicon
Ver menos
Requisitos do sistema: Software para leitura de arquivo em PDF
Marciano, Marina Angélica, 1987-
Orientador
Rodrigues, Clarissa Teles
Avaliador
Avaliação in vivo da migração local de íons bismuto e silício presentes em cimentos reparadores em contato com tecido conjuntivo e ósseo [recurso eletrônico]
Tamires Melo Francati
Avaliação in vivo da migração local de íons bismuto e silício presentes em cimentos reparadores em contato com tecido conjuntivo e ósseo [recurso eletrônico]
Tamires Melo Francati