This study describes the structural, porosity and morphological changes of porous polymer-derived ceramics obtained by pyrolysis of polysiloxane-clay composites, containing a pore former based on poly(dimethylsiloxane) and nickel acetate as nanostructure inductor. The composites were blended in a steel mold, thermally treated at 950 °C and 1500 °C (inert atmosphere). The increase of the temperature together with the presence of Ni resulted in more crystalline and porous ceramics and a higher ordering process of Cfree phase in the Ni-containing sample. The ceramics revealed a wide pore size distribution, from micro to macropores. At 950 °C the ceramic revealed the presence of pores and Ni- and C-rich islands dispersed on the fracture surface. However, at 1500 °C, nanowires with large aspect ratio, constituted by Si, C and O elements were generated. Thus, the presence of Ni associated to higher pores amount gave rise to an appropriate environment for the nucleation and growth of SiCO nanowires Ver menos

Este trabalho descreve as alterações estruturais, texturais e morfológicas de cerâmicas porosas derivadas de polímeros e obtidas pela pirólise de compósitos polissiloxano/argila, contendo formador de poros à base de poli(dimetilsiloxano) e acetato de níquel como indutor de nanoestruturas. Os compósitos foram obtidos a partir de molde de aço-inox, seguido por tratamento térmico a 950 °C e 1500 °C (atmosfera inerte). O aumento da temperatura associado com a presença de Ni resultou em cerâmicas mais cristalinas e porosas, além de maior ordenamento da fase de Clivre. As cerâmicas revelaram ampla faixa de tamanho de poros. Em 950 °C, foram gerados poros e ilhas ricas em Ni e C dispersas na superfície de fratura. Entretanto, a 1500 °C, foram obtidos nanofios com alta razão de aspecto constituídos de Si, C e O. Assim, a presença de Ni associada a maior quantidade de poros originou um ambiente apropriado para a nucleação e crescimento de nanofios de SiCO Ver menos