Title: Effect Of Different Surface Penetrating Sealants On The Roughness Of A Nanofiller Composite Resin
Author: Lopes M.B.
Saquy P.C.
Moura S.K.
Wang L.
Graciano F.M.O.
Sobrinho L.C.
Gonini Jr. A.
Abstract: This study evaluated the effectiveness of different sealants applied to a nanofiller composite resin. Forty specimens of Filtek Z-350 were obtained after inserting the material in a 6x3 mm stainless steel mold followed by light activation for 20 s. The groups were divided (n=10) according to the surface treatment applied: Control group (no surface treatment), Fortify, Fortify Plus and Biscover LV. The specimens were subjected to simulated toothbrushing using a 200 g load and 250 strokes/min to simulate 1 week, 1, 3 and 6 months and 1 and 3 years in the mouth, considering 10,000 cycles equivalent to 1 year of toothbrushing. Oral-B soft-bristle-tip toothbrush heads and Colgate Total dentifrice at a 1:2 water-dilution were used. After each simulated time, surface roughness was assessed in random triplicate readings. The data were submitted to two-way ANOVA and Tukey's test at a 95% confidence level. The specimens were observed under scanning electron microscopy (SEM) after each toothbrushing cycle. The control group was not significantly different (p>0.05) from the other groups, except for Fortify Plus (p<0.05), which was rougher. No significant differences (p>0.05) were observed at the 1-month assessment between the experimental and control groups. Fortify and Fortify Plus presented a rougher surface over time, differing from the baseline (p<0.05). Biscover LV did not differ (p>0.05) from the baseline at any time. None of the experimental groups showed a significantly better performance (p>0.05) than the control group at any time. SEM confirmed the differences found during the roughness testing. Surface penetrating sealants did not improve the roughness of nanofiller composite resin.
Editor: 
Rights: aberto
Identifier DOI: 10.1590/S0103-64402012000600011
Address: http://www.scopus.com/inward/record.url?eid=2-s2.0-84872968041&partnerID=40&md5=69170313ad72b20457a2f04d968a5c9e
Date Issue: 2012
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.