Title: Plasma Surface Treatment Of Alsl 4140 Steel For Improved Corrosion Resistance
Author: Mittelstadt F.G.
Franco C.V.
Muzart J.
De Souza A.R.
Cardoso L.P.
Abstract: Alloy AlSl 4140 steel was plasma-nitrided in a low-pressure abnormal glow discharge in 75% N2 + 25% H2 atmosphere (P = 3 torr and T = 540°C for 2 h) using a home-made laboratory reactor. The corrosion behaviour was evaluated in a chloride environment by potentiostatic and potentiodynamic polarization as a function of thermal treatment and cooling cycle. Results from potentiodynamic polarization in NaCl (3%) indicated the presence of a low anodic dissolution current of about 1 μA cm-2 for ionitrided steel having layers thickness >5 μm as compared to 0.1 A cm-2 for untreated steel. In addition, the open circuit potential shifted to noble potential clearly indicating that the ionitridation process is a very efficient process for corrosion protection of AlSl 4140 steel. Typical results obtained from samples oxidized during the cooling cycle showed an improvement in the corrosion resistance. The potential for pitting initiation and propagation as well as for pitting protection has been determined in a chloride environment. The use of electrochemical techniques as a control of standard parameters has been suggested. © 1996 Chapman & Hall.
Editor: 
Rights: fechado
Identifier DOI: 
Address: http://www.scopus.com/inward/record.url?eid=2-s2.0-0029771131&partnerID=40&md5=b1a893887b8c1153051a7c05f604ac4f
Date Issue: 1996
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
2-s2.0-0029771131.pdf616.38 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.