Title: Effect Of Refrigeration On Tensile Bond Strength Of Three Adhesive Systems.
Author: Spohr A.M.
Correr Sobrinho L.
Consani S.
Sinhoreti M.A.
Borges G.A.
Abstract: The purpose of this study was to investigate the tensile bond strengths of three adhesive systems applied to dentin at refrigerated and room temperatures. Ninety bovine incisor teeth were obtained, embedded in self-cured acrylic resin, abraded on a lathe under water spray and polished to 400 and 600 grit to form standardized dentin surfaces before randomly assigning to six groups (n = 15). The adhesive systems Scotchbond Multi-Purpose, Single Bond and Prime & Bond NT were applied to dentin according to the manufacturers' instructions at refrigerated temperature (4 degrees C) and at room temperature (23 degrees C), before bonding resin-based composite (Z 100). The specimens were stored in distilled water at 37 degrees C for 24 hours and submitted to tensile bond strength tests on a universal testing machine (EMIC DL-2000) at a crosshead speed of 0.5 mm/min. The resulting data were statistically analyzed using analysis of variance and Tukey's test. No statistical differences were found when the adhesive systems were applied at refrigerated and room temperatures. Scotchbond Multi-Purpose and Single Bond had significantly stronger tensile bond strengths than Prime & Bond NT at room and refrigerated temperatures (p < 0.01). Scotchbond Multi-Purpose and Single Bond were statistically similar. No adverse effects upon tensile bond strength were observed when adhesive systems were taken directly from refrigerated storage.
Editor: 
Rights: aberto
Identifier DOI: 
Address: http://www.scopus.com/inward/record.url?eid=2-s2.0-0035223182&partnerID=40&md5=718fd9211c957f3ba728e015227e5903
Date Issue: 2001
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
2-s2.0-0035223182.pdf28.71 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.