Title: Characterization Of Surface Nh3 +cl- Groups On Poly(styrene-co-boc-aminostyrene) Microspheres Obtained By Controlled Acidic Treatment
Author: Covolan V.L.
Galembeck F.
De Paula Leite C.A.
Ruggeri G.
Chiellini E.
Abstract: Different samples of aminated latex of poly(styrene-co-Boc-aminostyrene) microspheres with mean diameters varying from 0.7 to 1.0 μm were prepared by dispersion copolymerization of styrene (ST) and Boc-aminostyrene (Boc-AMST). The copolymer compositions determined by nuclear magnetic resonance ( 1H NMR) were Boc-AMST/ST 6.9/93.1 mol/mol % (BOC7 sample) and Boc-AMST/ST 31.3/68.7 mol/mol % (BOC30 sample). The average molecular weights determined by gel permeation chromatography were 126 kDa (BOC7 sample) and 51 kDa (BOC30 sample). The latex containing NH-carbo-tert-butoxy groups (NH-Boc) were treated with 2 M HCl in isopropyl alcohol/water (1:1 vol/vol), at 50°C for 3, 6, 9, 24, and 30 h, in order to control the extent of deprotection reaction of the NH-Boc. The deprotection reaction resulted in the formation of NH+ 3Cl- groups on the particle surfaces. The kinetic of the deprotection reaction was investigated by 1H NMR analyses and the yield varied from 20 to 40%. The resulting -NH+ 3Cl- groups on the microsphere surfaces were examined, in particular, by electron spectroscopy imaging (ESI) using an energy-filtered transmission electron microscope (EFTEM) that clearly demonstrated the presence of Cl on the particle surfaces. Scanning electron photomicrographs recorded for the above samples showed that the particle morphology was maintained after the acidic treatment. © 2004 Elsevier Inc. All rights reserved.
Rights: fechado
Identifier DOI: 10.1016/j.jcis.2004.01.070
Date Issue: 2004
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
2-s2.0-1642461346.pdf625.15 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.