|Title:||Influence Of Preheating On Api 5l-x80 Pipeline Joint Welding With Self Shielded Flux-cored Wire [influencia Del Precalentamiento En Las Propiedades De Uniones Soldadas De Acero Api 5l-x80 Soldadas Con Alambre Tubular Autoprotegido]|
|Abstract:||The present work refers to the characterization of API 5L-X80 pipeline joints welded with self-shielded flux cored wire. This process was evaluated under preheating conditions, with an uniform and steady heat input. All joints were welded in flat position (IG), with the pipe turning and the torch still. Tube dimensions were 762 mm in external diameter and 16 mm in thickness. Welds were applied on single V-groove, with six weld beads, along with three levels of preheating temperatures (room temperature, 100°C, 160°C). These temperatures were maintained as interpass temperature. The filler metal E71T8-K6 with mechanical properties different from parent metal was used in undermatched conditions. The weld characterization is presented according to the mechanical test results of tensile strength, hardness and impact test. The mechanical tests were conducted according to API 1104, AWS and ASTM standards. API 1104 and API 51 were used as screening criteria. According to the results obtained, it was possible to remark that it is appropriate to weld API 5L-X80 steel ducts with Self-shielded Flux Cored wires, in conformance to the API standards and no preheat temperature is necessary.|
|Appears in Collections:||Unicamp - Artigos e Outros Documentos|
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.