Title: Proposal Of A New G-bop Test To Evaluate Cracks In Weld Beads In Thin Sheets
Author: Silva J.H.F.
Fals H.C.
da Exaltacao Trevisan R.
Abstract: The objective of the present work is the evaluation of a proposal for a gapped bead-on-plate (G-BOP) test, used for study of hydrogen cracks in relatively thin sheets of welded steel. That new proposal consists of the replacement of the usual solid blocks by an assembly of blocks in such a way that the test can evaluate weld beads on thin sheets. Student t distribution is applied to examine the functionality of the proposed test. Weld metals were deposited with flux-cored wires E71T-1 and E71T8-K6, with diameters of 1.6 and 1.7 mm, respectively, under two different preheating temperatures. Metal susceptibility to hydrogen cracking was evaluated by the presence and percentage of cracks in the weld metal. In order to evaluate and verify the functionality of the new G-BOP test proposal, the following were examined: efficiency of the new test in inducing hydrogen cracks in the weld metal, result replicability, fracture modes present in cracks, and the cooling rate imposed on the welding zone. Results showed that the new G-BOP test proposal is viable; results were replicable and the test was efficient in inducing cracks in weld metal with a confidence of 90%. © ASM International 2008.
Rights: aberto
Identifier DOI: 10.1007/s11668-008-9199-5
Date Issue: 2009
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
2-s2.0-67649440920.pdf548.62 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.