Title: Influence Of Light-activation Protocol On Methacrylate Resin-composite Evaluated By Dynamic Mechanical Analysis And Degree Of Conversion
Author: Giorgi M.C.C.
Pistor V.
Mauler R.S.
Lima D.A.N.L.
Marchi G.M.
Aguiar F.H.B.
Abstract: The aim of this study was to evaluate the degree of conversion (DC) and to identify the viscoelastic properties: storage modulus (E'), loss modulus (E"), tangent delta (tan δ), and glass transition temperature (Tg) of a microhybrid resin-composite light-activated by three different protocols. A Filtek Z250 (3 M ESPE) shade A3 was inserted in a Teflon mold (21 mm × 5 mm × 1 mm for viscoelastic properties; and 5 mm × 1 mm for DC) and light-activated according to the following light-activation protocols: (S) 1,000 mW/cm2 × 19 s, (HP) 1,400 mW/cm2 × 14 s, and (PE) 3,200 mW/cm2 × 6 s, all set up to deliver 19 J/cm2. Viscoelastic properties was assessed by dynamic mechanical analysis (DMA) (n = 3), performed in single cantilever clamped mode. DC (n = 5) was measured by FTIR on top (T) and bottom (B) surfaces, and the data was submitted to a split-plot one-way ANOVA. For DC, there was a significant effect for surface factor and light-activation protocols factor. Top surface showed higher DC than B in all experimental conditions. Light-activation protocols S and HP resulted in higher DC than PE and were similar between them. Viscoelastic properties (E', E", tan δ, Tg) were not affected by light-activation protocols. It could be concluded that light-activation protocols influenced DC but not influenced the viscoelastic properties. © 2014 Springer-Verlag London.
Editor: 
Rights: fechado
Identifier DOI: 10.1007/s10103-014-1572-x
Address: http://www.scopus.com/inward/record.url?eid=2-s2.0-84901584656&partnerID=40&md5=2afc40997590a3f30aa2d00fa50d4953
Date Issue: 2014
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
2-s2.0-84901584656.pdf390.58 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.