Title: Influence of surface conditions and silane agent on the bond of resin to IPS Empress 2 ceramic
Author: Spohr, AM
Sobrinho, LC
Consani, S
Sinhoreti, MAC
Knowles, JC
Abstract: Purpose: The aim of this study was to evaluate the effect of different ceramic surface treatments on the tensile bond strength between IPS Empress 2 ceramic framework and Rely X adhesive resin cement, with or without the application of a silane coupling agent. Materials and Methods: One hundred twenty disks were made, embedded in resin, and randomly divided into six groups: group 1 = sandblasting (100 mum), no silanation; group 2 = sandblasting (100 pm), silane treatment; group 3 = sandblasting (50 pm), no silanation; group 4 = sandblasting (50 pm), silane treatment; group 5 = hydrofluoric acid etching, no silanation; and group 6 = hydrofluoric acid etching, silane treatment. The disks were bonded into pairs with adhesive resin cement. All samples were stored in distilled water at 37degreesC for 24 hours and then thermocycled. The samples were submitted to tensile testing. Results: The use of silane improved the bond strength in relation to the groups in which silane was not applied (P < .05). The most effective surface treatment was etching with 10% hydrofluoric acid, both with (25.6 MPa) and without silane application (16.4 MPa); these values showed a statistically significant difference compared to sandblasting with 50- and 100-mum Al(2)O(3). Sandblasting with 50-mum Al(2)O(3), with (11.8 MPa) and without silane (5.4 MPa), demonstrated significantly higher tensile bond strength than sandblasting with 100-pm Al(2)O(3), with (8.3 MPa) and without silane (3.8 MPa). Conclusion: Combined application of 10% hydrofluoric acid and silane enhanced the bond strength between the IPS Empress 2 ceramic framework and resin agent.
Country: EUA
Editor: Quintessence Publishing Co Inc
Rights: fechado
Date Issue: 2003
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000183116000012.pdf102.13 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.