Title: Tensile bond strength of dual curing resin-based cements to commercially pure titanium
Author: Schneider, R
de Goes, MF
Henriques, GEP
Chan, DCN
Abstract: Objectives. The aim of this study was to evaluate the tensile bond strength of dual curing luting resin cements to commercially pure titanium at 10 min and 24 h after removal of the oxide layer. Methods. One hundred and twenty titanium discs were obtained by casting and polishing with silicon carbide papers. The titanium discs were sandblasted with 50 mu m aluminum oxide, ultrasonic cleaned and bonded in pairs with the resin-based cements Panavia F and Rely X ARC at 10 min and 24 h after the sandblasting. The tensile test was performed with a crosshead speed of 0.5 mm/min in an Instron Universal testing machine. Results. The Rely X ARC reached the highest tensile strength value at 24 h after sandblasting (18.27 MPa), but there was no statistically significant difference between the two dual curing resin cements for both times tested. All specimens showed a mixture of cohesive fracture in the resin cement and adhesive failure. However, the predominant failure mode for Panavia F was cohesive in resin cement, and the Rely X ARC exhibited a greater proportion of specimens with adhesive failure between the alloy and resin luting cement at 10 min and 24 h. Significance. Both cements had, statistically, the same tensile bond strength. But in the fracture mode analysis, the adhesive predominant fracture mode of Rely X ARC cement indicates a premature clinical adhesive failure. On the other hand, the cohesive predominant fracture mode of Panavia F indicates a longer clinical adhesive bond with titanium. (C) 2005 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
Subject: titanium
resin-based cement
Country: Inglaterra
Editor: Elsevier Sci Ltd
Citation: Dental Materials. Elsevier Sci Ltd, v. 23, n. 1, n. 81, n. 87, 2007.
Rights: fechado
Identifier DOI: 10.1016/
Date Issue: 2007
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000243611800012.pdf715.92 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.