Title: Bond strength, biaxial flexural strength and flexural modulus of dentin bonding systems exposed to water
Author: Carvalho, AO
Carrilho, MRO
Rueggeberg, FA
Ambrosaho, GMB
Giannini, M
Abstract: Purpose: This study evaluated the effects of storage time on dentin bond strength, biaxial flexural strength, and flexural modulus of four adhesive systems. Materials and Methods: The following adhesive systems were tested: Easy Bond, Scotchbond SE, Single Bond Plus, and Scotchbond Multi-Purpose. Sixty human third molars were used for the microtensile bond strength test (n=15). The adhesives were applied to flat occlusal dentin surfaces according to the manufacturers' instructions and a Filtek Supreme resin composite block (6 mm high) was incrementally built up. After 24 h, the teeth were prepared for the bond strength test. The specimens were stored for one week, six months, and one year in distilled water. At the end of each storage period, the specimens were tested under tension (0.5 mm/min) until failure occurred. For the biaxial flexural test, resin discs of each adhesive (0.6 mm thick and 6.0 mm in diameter) were prepared in silicon molds (n=10). The discs were stored for the same storage periods in distilled water prior to testing in a universal testing machine (1.27 mm/min). Data were analyzed using two-way analysis of variance and Tukey's test (alpha=0.05). Results: Bond strength values decreased significantly after six months and one year of water storage only for Scotchbond SE (from 48.1 +/- 11.0 to 24.5 +/- 15.3 MPa after one year). The storage time did not affect the flexural strength or modulus for any adhesive tested. Conclusion: Water storage for six months or one year can reduce the dentin bond strength of adhesives; however, the results are product-dependent. No changes in flexural strength or modulus of the adhesives tested were observed after storage of any duration. (C) 2014 Published by Elsevier Ltd.
Subject: Bonding agents
Bond strength
Biaxial flexural strength
Modulus
Country: Inglaterra
Editor: Elsevier Sci Ltd
Rights: fechado
Identifier DOI: 10.1016/j.ijadhadh.2013.12.017
Date Issue: 2014
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.