Title: Adhesive systems and secondary caries formation: Assessment of dentin bond strength, caries lesions depth and fluoride release
Author: Peris, AR
Mitsui, FHO
Lobo, MM
Bedran-Russo, AKB
Marchi, GM
Abstract: Objectives. The present study evaluated the microtensile bond strength and caries formation on adhesive/dentin interfaces before and after dynamic chemical formation of secondary caries. Methods. Restorations were prepared on the dentin surface of 80 bovine incisors using four adhesive systems: two fluoride-free (Single Bond and Clearfil SE Bond) and two fluoride containing (Optibond Solo Plus and Clearfil Protect Bond). The restored teeth were then sectioned into multiple slabs that were further trimmed at the bonded interface to a crosssectional area of 1 mm(2). Half of the slabs were subjected to secondary caries formation using a pH cycling model (treated groups); while the other half was used as the control group (no pH cycling). The specimens designated for bond strength evaluation were subjected to microtensile bond strength test (mu TBS). Caries lesions formation was assesses by polarized light microscopy at different depths from the adhesive-dentin bonded interface. The fluoride ion concentration was evaluated using the de/remineralization solutions (De/Re). Results. No differences in mu TBS were observed among the adhesive systems in both the control and treated conditions. Secondary caries significantly reduced the values of mu TBS for all adhesives (p < 0.05). Optibond Solo Plus presented the lowest caries formation at 5 mu m depth. Fluoride concentrations present in the De/Re were less than 0.03 ppm, regardless of the adhesive system tested. Significance. Bond strength values significantly decreased after in vitro secondary caries formation. Fluoride present in adhesive systems is not capable of inhibiting secondary caries or maintaining bond strength values following caries formation. (c) 2006 Published by Elsevier Ltd on behalf of Academy of Dental Materials. All rights reserved.
Subject: fluoride releasing materials
microtensile bond strength
in vitro secondary caries
depth of caries formation
Country: Inglaterra
Editor: Elsevier Sci Ltd
Rights: fechado
Identifier DOI: 10.1016/j.dental.2006.02.001
Date Issue: 2007
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000244238700008.pdf1.05 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.