Title: Synthesis and structural characterization of nanometric ceria highly dispersed in SBA-15 with oxygen exchange capacity
Author: Silva, JMDE
Strauss, M
Maroneze, CM
Souza, ER
Gushikem, Y
Sigoli, FA
Mazali, IO
Abstract: Nanometric ceria-decorated SBA-15 was prepared using a route involving the impregnation of SBA-15 pores by a solution of cerium(III) 2-ethylhexanoate, followed by its thermal decomposition. According to XRF analysis, the number of successive impregnation-decomposition cycles (IDC) allows control of the CeO(2)/SiO(2) ratio in the final material, and also the tailoring of the nanoparticle size of the fluorite CeO(2) nanoparticles supported in the SBA-15, as confirmed by XRD, Raman and UV-Vis spectroscopies. The mean pore size of the SBA-15 decreases with successive IDC, as observed by N(2) adsorption-desorption, suggesting that CeO(2) nanoparticles are located inside the SBA-15 mesopores, as confirmed by TEM and HRTEM analyses. The degree of oxygen storage capacity (OSC) was measured by the number of hydrogen uptake from the temperature programmed reduction (H(2)-TPR). It was found that the value of hydrogen uptake of SBA-15 submitted to one IDC corresponds to 3344 mmol of O(2) per gram of CeO(2), whereas those of SBA-15 submitted to five and ten IDC were 1324 and 2769 mu mol of O(2) per gram of CeO(2), respectively.
Country: Inglaterra
Editor: Royal Soc Chemistry
Citation: Journal Of Materials Chemistry. Royal Soc Chemistry, v. 21, n. 39, n. 15678, n. 15685, 2011.
Rights: aberto
Identifier DOI: 10.1039/c1jm11476j
Date Issue: 2011
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000295278000083.pdf657.96 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.