Title: Susceptibility to hydrogen-induced cracking in H2S corrosion environment of API 5L-X80 weld metal
Author: Hilton, J
Fals, HC
Trevisan, RE
Abstract: The susceptibility to hydrogen-induced cracking in H2S environment of welded API X80 steel was Studied. The flux cored arc welding (FCAW) process was employed with E71-T1 and E71-T8K6 wires. The welding parameters were kept constant, but the samples were welded using different preheat temperatures (room temperature and 100 degrees C). The gapped bead-on-plate (G-BOP) test was used. The specimens of modified G-BOP tests were exposed to an environment saturated in H2S, as recommended by the NACE TM0284 standard. The weld beads were characterized by optical microscopy and the level of residual hydrogen in the samples was measured. The fracture surface areas of hydrogen-induced cracking were calculated and the fracture mode was discussed. It was found that the preheating temperature of 100 degrees C was enough to avoid cracking, even in the presence of H2S. It was also found that the E71-T8K6 wire was more susceptible to cracking,and the typical mixed-mode fracture was predominant in all samples
Subject: Welding
Hydrogen induced cracking
Cored wire
G-BOP test
Country: Espanha
Editor: Cenim
Citation: Revista De Metalurgia. Cenim, v. 45, n. 4, n. 267, n. 276, 2009.
Rights: aberto
Identifier DOI: 10.3989/revmetalm.0818
Date Issue: 2009
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000270052500003.pdf5.28 MBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.