Title: Effect of pre-heated dual-cured resin cements on the bond strength of indirect restorations to dentin
Author: Morais, A
dos Santos, ARA
Giannini, M
Reis, AF
Rodrigues, JA
Arrais, CAG
Abstract: This study evaluated the effects of resin luting agents (LA) polymerized using increased temperature on the in vitro microtensile bond strength (mu TBS) of indirect restorations to dentin. The occlusal dentin surfaces of 40 human third molars were exposed and flattened. The teeth were assigned to 8 groups (n = 5) according to the LA temperature (25 degrees C or 50 degrees C), curing mode (dual- or self-curing mode), and product (Excite DSC/Variolink II [VII] and XP Bond/Calibra [Cal]). The bonding agents were applied to the dentin surfaces according to manufacturers' instructions. For preheated groups, the LAs were heated to 50 degrees C, subsequently mixed on a heated stirrer surface, and applied to the previously heated pre-polymerized resin discs (2 mm thickness, TPH-Spectrum). The discs were bonded to the dentin surfaces, and the LAs were either exposed to a curing light according to manufacturers' instructions or allowed to self-cure. Specimens were stored in relative humidity at 37 degrees C for 7 days. Specimens were mesio-distally and bucco-lingually sectioned to obtain multiple bonded beams with a 1-mm(2) cross-sectional area for mu TBS testing. Data (MPa) were analyzed by 2-way ANOVA and Tukey's post hoc test (alpha = 5%) for each product. Specimen failure patterns were analyzed using a scanning electron microscope. VII groups showed higher mu TBS at 50 degrees C than at 25 degrees C regardless of curing mode (p = 0.05). Cal groups showed similar mu TBS at 25 degrees C and 50 degrees C in all activation modes. The use of some dual-polymerizing LAs at 50 degrees C may improve the mu TBS of indirect restorations to dentin.
Subject: Resin Cements
Temperature
Dental Bonding
Country: Brasil
Editor: Sociedade Brasileira De Pesquisa Odontologica
Rights: aberto
Date Issue: 2012
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000311862400014.pdf580.96 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.