Title: Carbon fiber/ceramic matrix composites: processing, oxidation and mechanical properties
Author: Pina, SRDO
Pardini, LC
Yoshida, IVP
Abstract: Ceramic matrix composites (CMC) have been considered in the last two decades to be alternative materials for highly demanding thermo-structural applications. Pre-ceramic polymers offer significant advantages for manufacturing these composites by the polymer impregnation method. In the present work, carbon fiber/silicon oxycarbide (C/SiCOy) composites were obtained by controlled pyrolysis of carbon fiber/ bridge polysilsesquioxane composites (COMPOSITE 1) followed by infiltration/pyrol ' ysis cycles with a polycyclic silicone network. The polysilsesquioxane showed high wettability and adhesion on the carbon fiber surface. An improvement of the thermo-oxidation resistance and a reduction of the porosity as a function of the number of polycyclic silicone infiltration cycles were observed. An extra improvement in the thermooxidation protection was found when the C/SiCOy composite was coated with a poly(phenylsilsesquioxane) layer (COMPOSITE 2). Shear properties for the composites showed a dependence on the nature of the matrix. The average in-plane shear strength and the shear modulus were 44.2 +/- 1.9 MPa and 2.2 +/- 0.5 GPa for the polymeric matrix composite (COMPOSITE 1), respectively. For the ceramic matrix composite (COMPOSITE 2) the values were 14.2 +/- 4.1 MPa and 15.0 +/- 2.0 GPa, respectively. The properties of the latter composite were also governed by the microstructure of the ceramic matrix.
Country: EUA
Editor: Springer
Rights: fechado
Identifier DOI: 10.1007/s10853-006-0688-1
Date Issue: 2007
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000247402300016.pdf398.33 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.