Title: Internal adaptation and some physical properties of methacrylate-based denture base resins polymerized by different techniques
Author: Ganzarolli, SM
de Mello, JAN
Shinkai, RS
Cury, AAD
Abstract: This study evaluated the internal adaptation, porosity, transverse and impact strength of three denture base polymers: (1) conventional heat-polymerized, (2) microwave-polymerized, and (3) injection-molded resins. Internal adaptation was measured by weighing a vinyl polysiloxane film reproducing the gap between the denture base and the metallic master model of an edentulous maxilla. The measurements were performed immediately after finishing and after 30-day storage in water. Porosity was evaluated by weighing each specimen in air and in water using an analytical scale balance. Transverse strength test (three-point bending test) was performed using a universal machine under axial load, at a crosshead speed of 5 mm/min. Impact strength test (Charpy's test) was performed with a 40 kJ/cm load. Data were analyzed by ANOVA and Tukey test (alpha = 0.05). Internal adaptation, porosity, transverse and impact strength varied according to the type of acrylic resin and the processing technique. The injection-molded resin showed better internal adaptation compared with the conventional heat-polymerized and the microwave-polymerized resins, particularly after 30 days, but there was no relevant improvement of porosity, transverse and impact strength. (c) Wiley Periodicals, Inc.
Subject: denture base resin
adaptation
porosity
transverse strength
impact strength
Country: EUA
Editor: Wiley-liss
Rights: fechado
Identifier DOI: 10.1002/jbm.b.30718
Date Issue: 2007
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000247612600022.pdf96.98 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.