|Title:||Influence of citrate/nitrate ratio on the preparation of Li0.5La0.5TiO3 nanopowder by combustion method|
|Abstract:||Preparation of nano-crystalline Li0.5La0.5TiO3 perovskite material using citrate nitrate redox reaction by the combustion technique is reported. The role of the ammonium nitrate concentration used to co-precipitate the Li0.5La0.5Ti-citrate precursor is revealed by ATD/TG, XRD, SEM-EDX and HRTEM techniques. Thermo-gravimetric analysis data show how the intensity of the exothermic peak associated with the citrate nitrate redox reaction decreases until disappearance as the citrate/nitrate molar ratio increases. The XRD study indicates that a single-phase cubic Li0.5La0.5TiO3 phase is formed at 350 degrees C when the citrate/nitrate ratio varies between 0.13 and 0.17. The formed Li0.5La0.5TiO3 powders show an average particle size of 15-20 nm. Electrochemical impedance spectroscopy technique reveals a relative high ionic conductivity inside the grain for the nanometric Li0.5La0.5TiO3 material, with values of around 10(-4) S/cm at room temperature. (C) 2013 Elsevier Ltd and Techna Group S.r.l. All rights reserved.|
|Subject:||Powders: chemical preparation|
|Editor:||Elsevier Sci Ltd|
|Citation:||Ceramics International. Elsevier Sci Ltd, v. 40, n. 1, n. 249, n. 256, 2014.|
|Appears in Collections:||Unicamp - Artigos e Outros Documentos|
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.