Title: Photoelastic evaluation of the effect of composite formulation on polymerization shrinkage stress
Author: Oliveira, KMC
Consani, S
Goncalves, LS
Brandt, WC
Ccahuana-Vasquez, RA
Abstract: We compared polymerization stress in two commercial composites and three experimental composites made using camphorquinone (CQ) and/or phenylpropanedione (PPD) as photoinitiators. The internal surfaces of photoelastic resin discs with cylindrical cavities were roughened and treated with adhesive. Composites were divided into five groups: two commercial composites (Filtek Silorane and Filtek Z250) and three experimental composites with CQ/amine, CQ/PPD/amine, and PPD/amine. Composites were photopolymerized inside cavities, and subjected to photoelastic analysis immediately and at 24 hours and 7 days later using a plane polariscope. Stress created by Silorane (3.08 +/- 0.09 MPa) was similar to that of Z250 (3.19 +/- 0.13 MPa) immediately after photopolymerization (p > 0.05). After 24 hours and 7 days, Z250 (3.53 +/- 0.15 and 3.69 +/- 0.10 MPa, respectively) showed higher stress than Silorane (3.19 +/- 0.10 and 3.16 +/- 0.10 MPa, respectively). Qualitative analysis immediately after photopolymerization showed composite/CQ promoted higher stress than PPD, but stress levels at other evaluated times were statistically similar, varying between 3.45 +/- 0.11 MPa and 3.92 +/- 0.13 MPa. At 24 hours and 7 days, Silorane created the lowest stress. All photoinitiators created comparable tensions during polymerization.
Subject: Composite Resins
Polymerization
Photoinitiators
Dental
Dental Stress Analysis
Country: Brasil
Editor: Sociedade Brasileira De Pesquisa Odontologica
Rights: aberto
Date Issue: 2012
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000311862500004.pdf603.13 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.