Title: Metallic brackets bonded with resin-reinforced glass lonomer cements under different enamel conditions
Author: Pithon, MM
dos Santos, RL
de Oliverira, MV
Ruellas, ACO
Romano, FL
Abstract: Objective: To assess the shear bond strength of metallic orthodontic brackets bonded with either Fuji Ortho or Ortho Glass LC resin-reinforced glass ionomer cements to enamel surfaces under different conditions, namely, enamel without etching, enamel conditioned with 37% phosphoric acid and enamel conditioned with Transbond Plus Self Etching Primer (TPSEP). Materials and Methods: One hundred and five bovine inferior incisors were divided into seven groups (n = 15). In group 1 (control) Transbond XT was used according to the manufacturer's recommendations. In groups 2, 3, and 4 all using Fuji Ortho LC, the brackets were bonded, respectively, to enamel nonetched, enamel etched with 37% phosphoric acid, and enamel etched with TPSEP. In groups 5, 6, and 7, the bonding was performed using Ortho Glass LC under the same enamel conditions observed in the other experimental groups. After 24 hours, shear bond strength tests were performed for all samples at a crosshead speed of 0.5 mm/min. Results: The results (MPa) showed no statistically significant difference between groups 1, 3, and 4 (P >.05). However, such groups were statistically superior to the others (P <.05). No statistically significant difference was observed between groups 2, 6, and 7 (P >.05). Group 5 showed the lowest shear strength value, which was also statistically inferior to the other groups (P <.05). Conclusions: Regardless of the enamel treatment, Fuji Ortho LC yielded shear strength values superior to those from Ortho Glass LC.
Subject: glass ionomer cement
shear strength
dental bonding
orthodontic brackets
Country: EUA
Editor: E H Angle Education Research Foundation, Inc
Rights: aberto
Date Issue: 2006
Appears in Collections:Artigos e Materiais de Revistas Científicas - Unicamp

Files in This Item:
File Description SizeFormat 
WOS000239016800025.pdf26.41 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.