Title: Compressive strength recovery by composite onlays in primary teeth. Substrate treatment and luting agent effects
Author: Borges, AFS
Correr, GM
Sinhoreti, MAC
Consani, S
Sobrinho, LC
Rontani, RMP
Abstract: Objectives: To evaluate 1% NaOCl treatment and two resin luting agent effects on compressive strength recovery in composite onlays on primary teeth and to analyze the fractures type. Methods: Forty sound primary molars crowns were prepared in the standard machine and randomly divided into four groups (n = 10): G1 (1% NaOCl/30 min + EnForce); G2 (without 1% NaOCl EnForce); G3 (1% NaOCl/30 min + Rely X); G4 (without 1% NaOCl + Rely X). The onlays were made using Z250 composite on plaster models. Ten sound teeth were used as control group (CG). All groups were submitted to compression mechanic test in a universal test machine INSTRON at 1 mm/min cross-head speed. After that, the data (kgf) were submitted to ANOVA test (alpha = 0.05). Finally, the fracture types were classified in a crescent scale (1-5) related with severity degree and submitted to Fisher's Exact Test (p < 0.05). Scanning electronic microscope analysis was done in order to illustrate the fractures sites. Results: The values of compressive strength of experimental groups did not differ each others neither from control group (p > 0.05). The results from fracture type showed that types 5 and 4 fractures (most severe) present the highest percentage to experimental groups. Conversely, the CG showed higher percentage of fracture types 2 and 3. Conclusions: This research found that the composite onlays recovered the compressive strength compared to sound teeth, regardless of the substrate treatment and cement agent used. Nevertheless, no group showed similar type of fractures to CG, which had more frequency of less severe fracture types. (c) 2005 Elsevier Ltd. All rights reserved.
Subject: composite resins
onlays
sodium hypochlorite
luting agents
compressive strength
Country: Inglaterra
Editor: Elsevier Sci Ltd
Rights: fechado
Identifier DOI: 10.1016/j.jdent.2005.11.003
Date Issue: 2006
Appears in Collections:Unicamp - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
WOS000240302900012.pdf729.02 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.