Title: Do new matrix formulations improve resin composite resistance to degradation processes?
Author: Fonseca, Andrea Soares Quirino da Silva
Gerhardt, Katia Maria da Fonseca
Pereira, Gisele Damiana da Silveira
Sinhoreti, Mario Alexandre Coelho
Schneider, Luis Felipe Jochims
Abstract: The aim of this study was to determine the degradation resistance of three new formulations-silorane-, Ormocer- and dimer-acid-based materials-and compare them to the traditional dimethacrylate-based materials. One silorane- (Filtek P90, P90), one Ormocer- (Ceram-X, CX), one dimer-acid- (N'Durance, ND) and two dimethacrylate-based (Filtek P60, P60; Tetric Ceram, TC) materials were investigated. Water sorption (Wsp) and solubility (Wsl) were determined after the materials were immersed in water for 28 days. Knoop hardness (KH) was determined before and after 24 h immersion in pure ethanol. The flexural-strength (FS) was determined by the bending test after one-week storage in a dry environment or after one-week immersion in pure ethanol. Data were submitted to analysis of variance (ANOVA) and Tukey's test (95%). The three new formulations showed lower Wsp than the dimethacrylate-based formulation. CX (0.50 ± 0.17%) and ND (0.72 ± 0.19%) exhibited the lowest Wsp, whereas P90 (0.02 ± 0.03%) and P60 (0.04 ± 0.03%) showed the lowest Wsl. All resins showed reduced Knoop hardness number (KHN) after ethanol immersion. P60 presented the lowest decrease in KH value (19 ± 5%). TC (48 ± 3%) and P90 (39 ± 9%) showed the highest KHN decrease after ethanol storage. The FS of CX, ND and TC were affected by ethanol storage. The new formulations did not improve the degradation resistance, as compared with the traditional methacrylate-based materials.
Subject: Solubility
Composite Resins
Water
Editor: Sociedade Brasileira de Pesquisa Odontológica - SBPqO
Rights: aberto
Identifier DOI: 10.1590/S1806-83242013000500005
Address: http://dx.doi.org/10.1590/S1806-83242013000500005
http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242013000500410
Date Issue: 1-Sep-2013
Appears in Collections:Artigos e Materiais de Revistas Científicas - Unicamp

Files in This Item:
File Description SizeFormat 
S1806-83242013000500410.pdf1.75 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.