Title: Avaliação in vitro da resistência à fadiga cíclica de limas reciprocantes tratadas com soluções irrigadoras a 37°C : In vitro evaluation of cyclic fatigue strength of reciprocating files treated with irrigation solutions at 37°C
Title Alternative: In vitro evaluation of cyclic fatigue strength of reciprocating files treated with irrigation solutions at 37°C
Author: Bohaienko, Renan Alves, 1990-
Advisor: Consani, Simonides, 1939-
Abstract: Resumo: Diversas técnicas e recursos mecânicos ganharam relevância na atividade clínica com a modernização da Odontologia. Dentre esses recursos, os motores elétricos são usados para as mais diversas indicações, como a terapia endodôntica. Assim, foram desenvolvidas limas endodônticas com ligas metálicas de diferentes composições e protocolos de aplicação para esses motores, objetivando reduzir o tempo clínico, melhorar o preparo mecânico dos canais radiculares e obter maior confiabilidade das limas para as mais diversas necessidades clínicas. O objetivo neste estudo foi avaliar o efeito de diferentes soluções aquecidas à temperatura de 37ºC sobre a resistência mecânica cíclica de limas de Niquel-Titânio (Ni-Ti). Foram avaliadas as soluções de hipoclorito de sódio (NaClO) a 5,25%, Digluconato de clorexidina gel a 2% e solução fisiológica, todas empregadas à temperatura de 37 ºC em limas com cinética reciprocante Reciproc Blue®, Prodesign S® e X1-Blue®. As diferentes limas foram imersas em cada solução por 10 minutos e mantidas em estufa à temperatura de 37ºC. Em seguida, foram submetidas ao teste de fadiga por flexão no laboratório de Endodontia da Faculdade de Odontologia de Bauru, USP, em dispositivo contendo canal com curvatura simulada de 60 graus e 5 mm de raio, imerso em água a 37ºC. Foram constituídos os seguintes grupos associando limas e soluções (n=15): RSF- Reciproc Blue® e solução fisiológica (Controle); RNa- Reciproc Blue® e NaClO 5,25%; RDC- Reciproc Blue® e Digluconato de clorexidina gel 2%; PSF- Prodesign S® e solução fisiológica (Controle); PNa- Prodesign S® e NaClO 5,25%; PDC- Prodesign S® e Digluconato de clorexidina gel 2%; XSF- X1-Blue® e solução fisiológica (Controle); XNa- X1-Blue® e NaClO 5,25% e XDC- X1-Blue® e Digluconato de clorexidina gel 2%. O teste mecânico de fadiga à flexão cíclica foi realizado até fratura das limas e o tempo cronometrado em segundos para calcular o número de ciclos. Os resultados foram submetidos ao teste estatístico ANOVA dois fatores e Bonferroni, seguido pelo teste de Tukey (?=5%) comparando parcelas subdivididas no programa SPSS 26.0 (SPSS, Chicago, IL,). Os resultados mostraram que não houve diferença significativa nos valores de resistência à fadiga cíclica das limas entre diferentes soluções e as marcas comerciais mostraram diferença significativa entre si. Não houve diferença significativa quanto ao número de ciclos entre as diferentes soluções quando comparadas ao controle para o mesmo grupo e houve diferença entre os números de ciclos e entre limas em cada solução. Em conclusão, o efeito das soluções irrigantes aquecidas a 37ºC sobre a fadiga cíclica de limas foi similar e as diferentes marcas de limas mostraram diferenças significativas entre si.

Abstract: Several techniques and mechanical resources have gained relevance in clinical activity with the modernization of the Dentistry. Among these resources, the electric motors are used for the most diverse indications, such as endodontic therapy. Thus, endodontic files were developed with metal alloys of different compositions and application protocols for these engines, aiming to reduce the clinical time, improve the cyclic mechanical preparation of the root canals and obtain greater reliability of the files for the most diverse clinical needs. The aim of this study was to evaluate the effect of different solutions heated to 37ºC on the cyclic mechanical fatigue of Ni-Ti files. The solutions of 5.25% NaClO, 2% chlorhexidine digluconate gel and physiological solution were employed at 37ºC in files with reciprocating kinetics Reciproc Blue ®, Prodesign S® and X1-Blue®. The files were immersed in each solution for 10 min and kept at 37ºC in a microbiological greenhouse. Then, they were submitted to the cyclic flexion fatigue test in the Endodontics laboratory of the Faculty of Dentistry of Bauru, USP, in a device containing a canal with simulated curvature of 60 degrees and 5 mm radius, and immersed in water at 37ºC. The following groups were formed associating files and solutions (n=15): RSF - Reciproc Blue® and physiological solution (Control), RNa – Reciproc Blue® and NaClO 5.25%, RCD - Reciproc Blue® and chlorhexidine digluconate gel 2%, PSF - Prodesign S® and physiological solution (Control), PNa - Prodesign S® and NaClO 5.25%. PDC - Prodesign S® and 2% chlorhexidine digluconate gel, XSF - X1-Blue® and physiological solution (Control), XNa - X1-Blue® and 5.25% NaClO and XDC - X1-Blue® and 2% chlorhexidine digluconate gel. The mechanical fatigue test was performed until the files failed and the time was measured in seconds to calculate the number of cycles. The results were subjected to the statistical test ANOVA two factors and Bonferroni, followed by the Tukey test (5%) comparing plots subdivided in the SPSS 26.0 program (SPSS, Chicago, IL,). The results showed that there was no significant difference in the values of strength to cyclic fatigue of files between different solutions and the different commercial brands showed a significant difference between them. There was no significant difference in the number of cycles between the different solutions when compared to the control for the same group, and there was a difference between the number of cycles and between files in each different solution. In conclusion, the effect of the different solutions at 37ºC on the files cyclic fatigue values was similar and the different file types showed significant differences among them.
Subject: Endodontia
Language: Português
Editor: [s.n.]
Citation: BOHAIENKO, Renan Alves. Avaliação in vitro da resistência à fadiga cíclica de limas reciprocantes tratadas com soluções irrigadoras a 37°C : In vitro evaluation of cyclic fatigue strength of reciprocating files treated with irrigation solutions at 37°C . 2021. 1 recurso online ( 47 p.) Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP.
Date Issue: 2021
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Bohaienko_RenanAlves_M .pdf1.46 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.