Type: DISSERTAÇÃO DIGITAL
Degree Level: Mestrado
Title: Efeito de silanos experimentais formulados com diferentes tio-uretanos na resistência da união e propriedades adesivas de pinos de fibra de vidro convencional e anatômico
Title Alternative: Effect of experimental silanes formulated with different thio- urethanes on bond strength and adhesive properties of convencional and anatomical fiberglass post
Author: Ramos, Roberta Araujo de Paula, 1994-
Advisor: Consani, Rafael Leonardo Xediek, 1974-
Abstract: Resumo: O estudo in vitro avaliou o efeito de silanos experimentais à base de tio-uretanos na fixação de pinos de fibra de vidro convencional ou anatômico aos condutos radiculares por meio da resistência ao cisalhamento por extrusão, padrão de falha e infiltração marginal. Os silanos experimentais foram sintetizados a partir da combinação do tiol-pentaeritritol tetra-3-mercaptopropionato (PETMP) com isocianatos 1,6-hexanodiol-diissocioso (HDDI) (alifático), ou 4,4¿-diisocianato de diciclo-hexilmetano (HDMI) (cíclico), ou 1,3-bis (1- isocianato-1-metiletil) (BDI) (aromático). Após tratamento endodôntico convencional com pinos de fibra de vidro convencional ou anatômico, as raízes bovinas foram separadas nos grupos (n=10): G1: pino de fibra de vidro convencional + silano comercial RelyX Ceramic Primer (controle); G2: pino de fibra convencional + silano experimental HDDI; G3: pino de fibra convencional + silano experimental HDMI; G4- pino de fibra convencional + silano experimental BDI; G5- pino de fibra de vidro anatômico + silano comercial RelyX Ceramic Primer (controle); G6: pino de fibra anatômico + silano experimental HDDI; G7: pino de fibra anatômico + silano experimental HDMI; G8- pino de fibra anatômico + silano experimental BDI. Todos os grupos foram submetidos às ciclagens mecânica (1,2 x 106 ciclos) e térmica (500 ciclos). Obteve-se duas fatias com 1 mm de espessura de cada terço radicular (cervical, médio e apical), uma submetida ao teste de resistência ao cisalhamento por extrusão (MPa) e padrão de falha (%) e outra submetida à infiltração marginal por corante (%) azul de metileno a 2% por sete dias. Os dados de padrão de falha e microinfiltração foram analisados por meio das frequências absolutas e relativas, e a resistência da união adesiva por meio de análise exploratória com o programa R (Core Team, 2019) com nível de significância de 5%. Os resultados revelaram maior resistência adesiva nos grupos G3 e G4 em todos os terços radiculares e no G2 no terço médio quando comparados com o controle (p<0,05) com pino convencional. Com pino anatômico, o G8 apresentou menor valor que o controle nos terços cervical e apical (p<0,05) e o G7 apresentou menor valor que o grupo controle no terço cervical (p<0,05). Os grupos G3 e G4 apresentaram valores significativamente maiores com o pino convencional do que com o pino anatômico em todos os terços (p<0,05). A maioria das amostras mostrou falha mista em todos os grupos. Houve predominância do escore 3 (+ que 2/3) com pino convencional, com exceção do grupo G3 no terço médio e nos grupos G2 e G4 no terço apical. Com pino anatômico houve aumento do escore 2 (1/3 e menos que 2/3) ou escore 1 (menos que 1/3), exceto nos terços cervical e médio do grupo PETMP-HDDI. Não foi observado escore 0 (sem infiltração). Conclui-se que os silanos experimentais à base de tio-uretanos promoveram maior resistência com pino convencional, a ocorrência de falha mista foi similar entre os grupos controle e silanos experimentais, e o pino de fibra de vidro anatômico reduziu a infiltração marginal em todos os grupos, exceto nos terços cervical e médio do grupo PETMP-HDDI

Abstract: The in vitro study evaluated the effect of experimental silanes based on thio-urethanes in restoring root tooth with conventional fiberglass (CFGP) or anatomical (AFGP) posts, through the bond strength, marginal micro-infiltration and failure pattern. Three experimental silanes were synthesized by combining thiol-pentaerythritol tetra-3-mercaptopropionate (PETMP) with different isocyanates such as 1,6-hexanediol-diisocious (HDDI) (aliphatic), or dicyclohexylmethane 4,4'-diisocyanate (HDMI) (cyclic), or 1,3-bis (1-isocyanate-1-methylethyl) (BDI) (aromatic). After conventional endodontic treatment, intra-canal preparation, and rehabilitation with a fiberglass post, the roots of the bovine teeth were separated into the following groups (n = 10): G1: CFGP + commercial silane (control); G2: CFGP + HDDI silane; G3: CFGP + HDMI silane; G4- CFGP + BDI silane; G5: AFGP + commercial silane Rely X Ceramic Primer (control); G6: AFGP + HDDI silane; G7: AFGP + silane HDMI; G8- AFGP + BDI silane. All groups were submitted to mechanical (1.2 x 106 cycles) and thermal (500 cycles) cycles. Two 1 mm thick slices were obtained from each root third (cervical, middle and apical), one submitted to the bond strength test (BS) and failure pattern (FP) and the other submitted to marginal micro-infiltration (MI) through 2% methylene blue dye for seven days. The data obtained from FP and MI were analyzed descriptively using absolute and relative frequencies, while BS was subjected to exploratory analysis with the aid of the R program (Core Team, 2019) at a significance level of 5%. The results revealed a higher BS in groups G3 and G4 in all roots thirds and in group G2 in middle third for CFGP when compared with the control group (p <0.05). When using AFGP, G8 had a lower BS than the control group, in the cervical and apical thirds (p <0.05) and G7 had a lower BS than the control group, in the cervical third (p <0.05). Groups G3 and G4 showed significantly higher BS with the CFGP than with the AFGP in all thirds (p <0.05). Most of the samples had mixed (dentin-cement adhesive) failure in all groups. There was a predominance of score 3 (interface stained more than 2/3) in CFGP, except for the middle third in G3 group and the apical third in G2 and G4 groups. In AFGPs there was a predominance of score 2 (interface stained more than 1/3 and less than 2/3) in all groups. No score 0 was observed (without dye infiltration). Thus, it is concluded that the experimental silanes based on thio-urethanes promoted greater BS in CFGP, the mixed failure pattern found in the control group was maintained in the groups with experimental silanes and the anatomy of the fiberglass posts reduced the MI in all groups
Subject: Silano
Endodontia
Resistência de união
Pinos dentários
Cimentos dentários
Language: Português
Editor: [s.n.]
Citation: RAMOS, Roberta Araujo de Paula. Efeito de silanos experimentais formulados com diferentes tio-uretanos na resistência da união e propriedades adesivas de pinos de fibra de vidro convencional e anatômico . 2020. 1 recurso online ( 76 p.) Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: http://www.repositorio.unicamp.br/handle/REPOSIP/355716. Acesso em: 12 Mar. 2021.
Date Issue: 2020
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Ramos_RobertaAraujoDePaula_M.pdf2.03 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.