Title: Influence of crosshead speed on failure load and failure mode of restored maxillary premolars
Author: Naves, Lucas Zago
Silva, Gisele Rodrigues da
Correr-Sobrinho, Lourenço
Costa, Ana Rosa
Valdivia, Andréa Dolores Correia Miranda
Soares, Carlos José
Abstract: We analyzed the effect of the crosshead speed of an applied load on failure load and failure mode of restored human premolars. Fifty intact, noncarious human premolars were selected. Class II mesio-occlusodistal preparations were made with a water-cooled high-speed preparation machine, and the teeth were restored with composite resin. The specimens were divided into five groups (n = 10 each) and tested individually in a mechanical testing machine, in which a 6.0-mm-diameter steel cylinder was mounted to vary the crosshead speed: v0.5: 0.5 mm/min; v1: 1.0 mm/min; v2.5: 2.5 mm/min; v5: 5.0 mm/min; and v10: 10.0 mm/min. The cylinder contacted the facial and lingual ridges beyond the margins of the restorations. Peak load to fracture was measured for each specimen (N). The means were calculated and analyzed with one-way analysis of variance followed by Tukey's test (a = 0.05). The mean load at failure values were (N) as follows: v0.5, 769.4 ± 174.8; v1, 645.2 ± 115.7; v5, 614.3 ± 126.0; v2.5, 609.2 ± 208.1; and v10, 432.5 ± 136.9. The fracture modes were recorded on the basis of the degree of the tooth structural and restorative damage: (I) fracture of the restoration involving a small portion of the tooth; (II) fractures involving the coronal portion of the tooth with cohesive failure of the composite resin; (III) oblique tooth and restoration fracture with periodontal involvement; and (IV) vertical root and coronal fracture. Varying crosshead speeds of 0.5–5.0 mm/min did not influence the failure load of restored maxillary premolars; however, increasing the crosshead speed to 10 mm/min decreased the failure load values and the degree of tooth structural damage
Subject: Resinas compostas
Country: Brasil
Editor: Sociedade Brasileira de Pesquisa Odontológica
Rights: Aberto
Identifier DOI: 10.1590/1807-3107BOR-2016.vol30.0003
Address: https://www.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242016000100206
Date Issue: 2016
Appears in Collections:FOP - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
000378324000003.pdf311.13 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.