Title: Desempenho físico-químico de infiltrantes experimentais e comercial : um estudo in vitro e in situ = Physicochemical performance of experimental and commercial infiltrants : an in vitro and in situ study
Title Alternative: Physicochemical performance of experimental and commercial infiltrants : an in vitro and in situ study
Author: Ribeiro, Mariana Dias Flor, 1991-
Advisor: Marchi, Giselle Maria, 1970-
Abstract: Resumo: Objetivos: Desenvolver infiltrantes experimentais contendo sal de difeniliodônio (DFI) e quitosana em diferentes concentrações e avaliar seu desempenho físico-químico in vitro (Cap. 1) e in situ (Cap. 2) em comparação com o infiltrante comercial. Materiais e métodos: Foram desenvolvidos 9 infiltrantes experimentais contendo TEGDMA e BisEMA, variando a concentração do DFI em 0; 0,5; 1 mol% e quitosana em 0; 0,12 e 0,25% - em peso, que foram comparados com o infiltrante comercial Icon® (controle positivo). A formulação foi realizada em ambiente com iluminação e temperatura controlados. Para o estudo in vitro, foram utilizados corpos de prova de infiltrantes polimerizados e realizados testes de Módulo de Elasticidade (n=10), Resistência à Flexão (n=10), Grau de Conversão (n=5), Sorção (n=5) e Solubilidade (n=5); e para o teste de Ângulo de contato (n=6) foram utilizados blocos de esmalte humano dental polido e infiltrantes não polimerizados. Para o estudo in situ, 132 blocos de esmalte humano dental (n=12/grupo) foram confeccionados e submetidos à simulação de lesão inicial de cárie. As amostras foram aleatorizadas com base na microdureza inicial do esmalte e divididas em 11 grupos de tratamento (9 infiltrantes experimentais, infiltrante comercial como controle positivo e grupo sem tratamento como controle negativo) e foram realizados os testes de Rugosidade (n=3), Área (n=3), Morfologia e Projeção Superficial com Microscópio de Força Atômica (n=3), Análise microbiológica por Teste de Unidades Formadoras de Colônias (UFC/mL; n=5) e Profundidade de Penetração (n=3) com Microscópio Confocal de Varredura à Laser. Os dados foram analisados por meio de modelos lineares generalizados e ANOVA one-way com post-hoc de Tukey e pelo teste de Dunnet (alfa=0.05). Resultados: In vitro - Grupos de infiltrantes contendo a mistura de DFI 1% e quitosana 0.12% e 0.25% tiveram melhores resultados de módulo de elasticidade, resistência à flexão e grau de conversão em comparação com o produto comercial Icon®. Porém, para sorção, solubilidade e ângulo de contato, o Icon® teve o melhor desempenho. In situ - Não houve diferença significativa entre os onze grupos quanto atividade microbiológica (UFC/mL), rugosidade e área (p<0.05). A profundidade de penetração foi significativamente maior no grupo sem tratamento do que no grupo com 0.5% de DFI e 0.25% de Quitosana (p<0.05). Conclusão: Os infiltrantes experimentais contendo sal de iodônio e quitosana testados apresentam similaridade em comparação com o infiltrante comercial Icon®

Abstract: Objectives: To development experimental infiltrants containing diphenyliodonium salt (DPI) and chitosan in different concentrations and to evaluate their physicochemical performance in vitro (Chapter 1) and in situ (Chapter 2) in comparison with the commercial infiltrant. Material and methods: Nine experimental infiltrants containing TEGDMA and BisEMA were prepared, varying the DPI concentration by 0; 0.5; 1 mol% and chitosan at 0; 0.12 and 0.25% - by weight, which were compared with the commercial Icon® infiltrant. The formulation was performed in environment with controlled lighting and temperature. For the in vitro analyses, polymerized infiltrants specimens were used and Elastic Modulus (n = 10), Flexural Strength (n = 10), Degree of Conversion (n = 5), Sorption (n = 5) and Solubility (n = 5) tests were performed; and for the Contact Angle test (n = 6), polished dental human enamel blocks and unpolymerized infiltrants were used. For the in situ study, 132 blocks of human dental enamel (n = 12 / group) were made and submitted to the simulation of initial caries lesion. Samples were randomized based on initial enamel microhardness and divided into 11 treatment groups (9 experimental infiltrants, commercial infiltrant as positive control and untreated group as negative control) and the Roughness (n = 3), Area (n=3), Morphology and Surface Projection (n = 3) with Atomic Force Microscope, Microbiological Analysis by Colony Forming Test (CFU / mL; n = 5) and Penetration Depth (n = 3) with Confocal Laser Scanning Microscope tests were performed. Data were analyzed using generalized linear models and one-way ANOVA with Tukey post-hoc and Dunnet's test (alfa = 0.05). Results: In vitro - Infiltrants groups containing 1% DPI and 0.12% and 0.25% chitosan in the blend had better results of elastic modulus, flexural strength and degree of conversion compared to the commercial Icon® infiltrant. In situ - There was no significant difference between the eleven groups regarding microbiological activity (CFU/mL), roughness and area (p <0.05). Penetration depth was significantly greater in the untreated group than in the 0.5% DPI and 0.25% Chitosan group (p <0.05). Conclusion: The experimental infiltrants containing iodonium salt and chitosan tested are similar when compared to the commercial infiltrant Icon®
Subject: Gomas e resinas sintéticas
Técnicas in vitro
Hibridização in situ fluorescente
Oniocompostos
Quitosana
Language: Multilíngua
Editor: [s.n.]
Citation: RIBEIRO, Mariana Dias Flor. Desempenho físico-químico de infiltrantes experimentais e comercial: um estudo in vitro e in situ = Physicochemical performance of experimental and commercial infiltrants : an in vitro and in situ study. 2019. 1 recurso online ( 69 p.) Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Campinas, SP.
Date Issue: 2019
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Ribeiro_MarianaDiasFlor_D.pdf2.76 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.