Title: Análise de três diferentes protocolos de remoção de pinos de fibra de vidro com pontas ultrassônicas : estudo ex vivo
Title Alternative: Analisys of three different ultrassoinic tip fiberglass posts removal protocol : ex vivo study
Author: Honda, Ricardo, 1990-
Advisor: Almeida, Jose Flavio Affonso de, 1979-
Abstract: Resumo: A utilização de pinos de fibra de vidro tornou-se cada vez mais comum na reabilitação dos elementos dentários. Com isso, há um aumento das situações que exigem a sua remoção, podendo ocorrer após a fratura dos pinos ou do insucesso da terapia endodôntica. Entretanto, desgastes exagerados, desvios, perfurações e danos aos tecidos de suporte estão sujeitos a acontecer. Dessa forma, o objetivo deste estudo ex vivo foi avaliar três protocolos de remoção de pinos de fibra de vidro através do desgaste utilizando pontas ultrassônicas lisas (TRA12), acopladas a um adaptador. Vinte e quatro dentes monorradiculares de diferentes grupos e com características semelhantes foram preparados e divididos em 3 grupos (n=8): G20 ¿ ciclos com duração de 20 segundos de aplicação sem refrigeração nesse período, G40 ¿ ciclos de 40 segundos de aplicação sem refrigeração nesse período e G20a ¿ ciclos de 20 segundos de aplicação com refrigeração do próprio aparelho durante esse período. Foram analisados o tempo total necessário para a remoção dos pinos, a variação da temperatura externa em diferentes regiões da raiz e a análise microtomógrafa da quantidade de desgaste promovido na dentina, de material que permaneceu aderido as paredes do canal radicular e o surgimento ou a propagação de trincas radiculares. O estudo considerou um nível de significância "alfa"= 5%. Em relação ao tempo de remoção, o grupo G40 foi mais rápido que o G20, e o G20a foi semelhante aos demais. O grupo G20a apresentou menores valores de aumento de temperatura na região cervical, no entanto não foi observada diferença estatística entre os grupos na porção apical. Nenhum dos grupos resultou em variações de temperatura condizentes com a geração de danos biológicos. Todos os grupos deixaram quantidades significativas de material aderido as paredes do canal radicular. Os três protocolos testados podem criar ou propagar trincas radiculares. A utilização do ultrassom demonstrou ser um método viável quando é utilizado em intervalos de tempo controlados, independentemente da associação de um regime de refrigeração. Além disso, há necessidade de um método complementar para melhorar a remoção dos resíduos de materiais que permaneceram aderidos as paredes do canal radicular

Abstract: The use of fiberglass posts has become increasingly common in dental element rehabilitation. Thus, there is an increase in situations that require their removal, which may occur after fracture of the posts or failure of endodontic therapy. However, excessive wear, deflection, perforation, and damage to supporting tissues are likely to occur. Thus, the objective of this ex vivo study was to evaluate three protocols for fiberglass post removal through wear using flat ultrasonic tips (TRA12) coupled to an adapter. Twenty-four monoradicular teeth of different groups and with similar characteristics were prepared and divided into 3 groups (n = 8): G20 - cycles of 20 seconds of application without cooling in this period, G40 - cycles of 40 seconds of application without cooling during this period and G20a - cycles of 20 seconds of application with cooling of the device itself during this period. The total time required for the removal of the pins, the variation of the external temperature in different root regions and the microtomography analysis of the amount of wear promoted on the dentin, of the material that remained adhered to the root canal walls and the appearance or propagation were analyzed of root cracks. The study considered a significance level 'alfa' = 5%. Regarding the removal time, group G40 was faster than G20, and G20a was similar to the others. Group G20a presented lower temperature increase values in the cervical region, however no statistical difference was observed between the groups in the apical portion. Neither group resulted in temperature variations consistent with the generation of biological damage. All groups left significant amounts of material adhered to the root canal walls. The three protocols tested can create or propagate root cracks. The use of ultrasound has proven to be a viable method when used at controlled time intervals, regardless of the association of a refrigeration regime. In addition, there is a need for a complementary method to improve the removal of material residues that remained adhered to the root canal walls
Subject: Endodontia
Ultrassom
Microtomografia por raio-X
Canal radicular
Language: Português
Editor: [s.n.]
Citation: HONDA, Ricardo. Análise de três diferentes protocolos de remoção de pinos de fibra de vidro com pontas ultrassônicas: estudo ex vivo. 2019. 1 recurso online ( 89 p.) Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP.
Date Issue: 2019
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Honda_Ricardo_M.pdf1.32 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.