Title: Influence of 3-month simulated pulpal pressure on the microtensile bond strength of simplified resin luting systems
Author: Bacchi, Atais
Abuna, Gabriel
Babbar, Ashvin
Coelho Sinhoreti, Mario Alexandre
Feitosa, Victor Pinheiro
Abstract: To assess the influence of simulated pulpal pressure (SPP) on the microtensile bond strength (mu TBS) of four simplified luting strategies to indirect composite restorations. Dentin disks from 40 human molars were prepared and treated with 4 different techniques: (1) SB+ARC: two-step etch-and-rinse adhesive + conventional dual-curing resin cement (Adper Single Bond 2 + RelyX ARC, 3M ESPE); (2) ED+PAN: self-etching primer + conventional dual-curing resin cement (ED Primer + Panavia F2.0, Kuraray Medical); (3) S3+ PAN: one-step self-etching adhesive (Clearfil S3, Kuraray) + Panavia F2.0; (4) U200: self-adhesive resin cement (RelyX U200, 3M ESPE). Pre-made indirect composite restorations (Filtek Z100, 3M ESPE) were luted onto the specimens. The luted specimens were cut into resin-dentin beams and the mu TBS was tested after two different aging regimes: water storage at 37 degrees C for one week (control) or three months under 20 cm H2O simulated pulpal pressure (SPP). The mu TBS data was analyzed with two-way ANOVA and Tukey's test (p < 0.05). SB+ARC showed significantly higher mu TBS after both aging regimes (p < 0.001). The statistically significantly lowest mu TBS was measured for control S3+ PAN and U200 after 3 months SPP (p < 0.001). S3+ PAN was the only group not negatively affected by SPP (p = 0.699). Two-step etch-and-rinse adhesives associated with dual-curing conventional resin cements may achieve the highest mu TBS, even after 3 months of SPP. The one-step self-etching adhesive along with the dualcuring conventional resin cement was able to maintain bond stability
Subject: Adesivos dentinários
Esmalte dentário
Country: Reino Unido
Editor: Quintessence Publishing
Rights: Fechado
Identifier DOI: 10.3290/j.jad.a34414
Date Issue: 2015
Appears in Collections:FOP - Artigos e Outros Documentos

Files in This Item:
There are no files associated with this item.

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.