Title: Effect of vanadium addition on the surface roughness and fatigue crack propagation in a railroad wheel using twin disc wear test
Author: Rezende, A.B.
Amorim, G.A.
Minicucci, D.J.
Fonseca, S.T.
Mei, P.R.
Abstract: To verify the effect of 0.13 % vanadium addition (% in weight) on the wear resistance of a railroad wheel steel with 0.7 % carbon, twin-disc rolling-sliding test were performed. These two steels were named 7V and 7C. The test discs were analyzed to verify the superficial conditions and wear mechanisms using SEM (Scanning Electron Microscopy) and roughness measurements. After 100,000 cycles running it was concluded that without the presence of debris, the 7V steel presented a reduction in 35 % the mass loss compared to 7C steel. For the 7V steel, in the test without debris, the discs presented small cracks (10 μm long), very near (3 μm deep) the surface, but in the test with the presence of debris, the disc surfaces presented delaminated material and long cracks (100 μm long) faraway from surface (up to 72 μm deep). The presence of debris also increased the roughness parameters in 7V steel: average Rz jumped from near 6 μm in the steel without debris to near 26 μm in the steel with debris
Subject: Fadiga
Vanádio
Country: Suiça
Editor: Scientific.Net
Rights: Fechado
Identifier DOI: 10.4028/www.scientific.net/DDF.391.66
Address: https://www.scientific.net/DDF.391.66
Date Issue: 2019
Appears in Collections:FEM - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
2-s2.0-85062732362.pdf6.72 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.