Title: Efeito da fumaça de cigarro nas propriedades físicas de resinas compostas convencionais e Bulk-fill : Effect of cigarette smoke on physical properties of conventional and Bulk-fill composite resins
Title Alternative: Effect of cigarette smoke on physical properties of conventional and Bulk-fill composite resins
Author: Theobaldo, Jéssica Dias, 1989-
Advisor: Aguiar, Flavio Henrique Baggio, 1977-
Abstract: Resumo: Objetivo: Avaliar o efeito da exposição de resinas compostas convencionais, (Capítulo 1) e resinas do tipo bulk-fill (Capítulo 2) à fumaça de cigarro (FC) nas propriedades de cor (Capítulo 1 e 2), rugosidade e brilho (Capítulo 2). Materiais e Métodos: No Capítulo 1, foram confeccionados discos de resina com 5 de diâmetro por 2 mm de espessura [Filtek Z250XT (3M ESPE) e Filtek Z350XT (3M ESPE)], os quais foram expostos à cigarros com diferentes concentrações dos principais componentes do cigarro [alcatrão, nicotina, monóxido de carbono (CO)]: Marlboro Red (MR) > Marlboro Blue Ice (MBI) > Marlboro Filter Plus (MFP) > Marlboro Silver Light (MSL) e controle (sem exposição) (n=10). As amostras foram armazenadas em saliva artificial, a 37 oC. Os espécimes foram expostos à 20 cigarros por dia, durante 5 dias. A análise da cor (delta E, L*, a*, b*) foi realizada nos tempos: baseline e após exposição à FC. Os dados foram submetidos à ANOVA dois fatores e Teste de Tukey. A análise de regressão linear (RL) analisou a influência do alcatrão, nicotina e CO nas variáveis de cor (a = 0,05). No Capítulo 2, utilizou-se discos de resina (10 x 2 mm; n=10), sendo avaliadas: Filtek Z250XT (3M ESPE, Controle); Filtek One bulk-fill (3M ESPE, FOBF); Tetric N-Ceram bulk-fill (Ivoclar Vivadent, TNCBF) e Aura bulk-fill (SDI - ABF). A análise de cor (delta E, delta L*,delta a*, delta b*), rugosidade (Ra) e brilho foram realizadas nos tempos: baseline e após exposição à FC (10 maços - Marlboro Red). Os dados foram submetidos a análise de medidas repetidas e Tukey teste (Ra e brilho); ANOVA um fator (delta L*, delta a*, delta b* e delta E) e Teste de Tukey (alfa <0,05). Resultados: No Capítulo 1, as variáveis de cor delta L*, delta a* e delta E, para ambas resinas, diferiram estatisticamente do controle (p<0,05), independentemente do tipo de cigarro, apresentando maiores valores. A análise de RL mostrou relação significativa entre os parâmetros de cor (L*, a*, b* e delta E) e os principais componentes do cigarro (p<0,05), sendo maior nas resinas nanoparticuladas. No Capítulo 2, para delta L* e delta E, todas as resinas bulk-fill apresentaram maior variação diferindo estatisticamente do controle. Entre as resinas, ABF apresentou maior variação (p<0,05). Para Ra, após FC, ABF apresentou menores valores (p<0,05) quando comparada aos valores iniciais. Para brilho todos os grupos apresentaram aumento após FC, sendo estatisticamente diferentes do controle. Conclusão: Cigarros com maiores concentrações de alcatrão, nicotina e CO promovem o aumento na pigmentação das resinas compostas. A pigmentação de resinas compostas convencionais pelo cigarro é concentração - dependente da fumaça de cigarro e é mais evidente em resinas nanoparticuladas. Resinas nanoparticuladas e do tipo bulk-fill são mais susceptíveis ao manchamento pela fumaça do cigarro quando comparadas à resina microhíbrida

Abstract: Objective: To evaluate the effect of exposure to conventional composite resins (Chapter 1) and bulk-fill resins (Chapter 2) to cigarette smoke on physical properties such as color (Chapter 1 e 2), roughness (Ra) and gloss (Chapter 2). Materials and Method: In Chapter 1, resin discs with 5 mm of diameter and 2 mm of thickness were obtained (Filtek Z250XT (3M ESPE); Filtek Z350XT (3M ESPE)) and exposed to cigarettes with different concentrations of main cigarette components [tar, nicotine, carbon monoxide (CO)]: Marlboro Red (MR)>Marlboro Blue Ice (MBI)>Marlboro Filter Plus (MFP)>Marlboro Silver Light (MSL) and control (without exposure) (n=10). All samples were stored in artificial saliva at 37 oC. The specimens were exposed to 20 cigarettes/day for 5 days. Color analysis (delta E, L*, a*, b*) was performed at two times: at the baseline and after CS exposure. The data were submitted to a two-way ANOVA and Tukey¿s test. Linear regression (LR) was used to analyze the influence of tar, nicotine and CO on the color variable (a=0.05). In Chapter 2, resin discs (10 x 2 mm) were prepared for each restorative material used (n=10): Filtek Z250XT (3M ESPE, control), Filtek One Bulk-Fill (3M ESPE, FOBF), Tetric N-Ceram Bulk-Fill (Ivoclar Vivadent, TNCBF) and Aura Bulk-Fill (SDI - ABF). The color (delta E, delta L*, delta a*, delta b*), Ra and gloss analyses were performed at two times: at the baseline and after CS exposure (10 pack of cigarettes ¿ Marlboro Red, (Philip Morris Brazil Ind. e Com)). The data were analyzed with repeated measures ANOVA and Tukey test (Ra and gloss); a one-way ANOVA ( delta L*, delta a*, delta b* and delta E); and Tukey¿s test (alfa 0.05). Results: In Chapter 1, for all analyses, control groups did not differ. For delta E, delta L* and delta a*, both resins showed statistical difference from the control (p<0.05), regardless of tobacco type, presented the highest values. LR analysis showed a significant relationship between all color parameters (L*, a*, b* and delta E) and the tar, nicotine and CO concentration, were higher in nanofilled resins comparing to microhybrid resins. In Chapter 2, for delta L* and delta E, all bulk-fill resins differed statistically from the control, which presented the lower value. Among resins, ABF showed greater variation (p<0.05). For Ra, after CS exposure, only ABF presented lower values (p<0.05) than the baseline. For gloss, all groups presented an increase in values after exposure to CS, and they were statistically different from the control. Conclusion: Cigarettes with higher concentrations of tar, nicotine and CO promote an increase in pigmentation of the composite resins. The pigmentation of conventional composite resins by the cigarette is concentration-dependent at cigarette smoke and is most evident in nanofilled resins. Nanofilled and bulk-fill resins are more susceptible to cigarette smoke staining when compared to the microhybrid resin
Subject: Resinas compostas
Hábito de fumar
Propriedades físicas
Language: Multilíngua
Editor: [s.n.]
Citation: THEOBALDO, Jéssica Dias. Efeito da fumaça de cigarro nas propriedades físicas de resinas compostas convencionais e Bulk-fill : Effect of cigarette smoke on physical properties of conventional and Bulk-fill composite resins . 2019. 1 recurso online ( 86 p.) Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP.
Date Issue: 2019
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Theobaldo_JessicaDias_D.pdf2.23 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.