Title: Metallic glass formation upon rapid solidification of Fe60Cr8Nb8B24 (at%) alloy through LASER cladding and remelting
Author: Carvalho, Marcos Fernandes de
Riva, Rudimar
Fogagnolo, João Batista
Kiminami, Cláudio Shyinti
Afonso, Conrado Ramos Moreira
Abstract: Fe60Cr8Nb8B24 (at%) amorphous powder and ingot were submitted to LASER cladding and remelting process, respectively. Fe-based coatings were produced using different LASER processing parameters and characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and Vickers microhardness. All coatings obtained by LASER cladding (LC) and layers obtained by LASER surface remelting (LSR) with shorter and median interaction times (scanning speeds of 16.7 and 66.7mm/s), irrespective of overlap value, presented peaks of the crystalline phases α-Fe, Fe2B and the FeNbB intermetallic. In addition, layers obtained by LSR with shorter interaction time (150mm/s), in general, presented only peaks of the α-Fe and Fe2B phases, except that produced with overlap value of 20%, more amorphous. SEM results showed that, regardless of LASER process, the coatings presented cracks, some pores and FeNbB intermetallic phase. All coatings obtained by LC and that obtained with shorter interaction time, by LSR, showed a Vickers microhardness, 1086 to 1329HV and 2161 to 2294HV, respectively, significantly higher than the substrates, AISI steel: 170HV and Fe-Cr-Nb-B: 1921HV
Subject: Vidro
Revestimentos
Lasers
Country: Brasil
Editor: UFSCar/Departamento de Engenharia de Materiais
Rights: Aberto
Identifier DOI: 10.1590/1980-5373-mr-2017-0732
Address: https://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392017000800580
Date Issue: 2017
Appears in Collections:FEM - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
S1516-14392017000800580.pdf3.28 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.