|Title:||Orthorhombic martensite formation upon aging in a Ti-30Nb-4Sn alloy|
|Author:||Salvador, Camilo A.F.|
Lopes, Eder S.N.
Ospina, Carlos A.
|Abstract:||The characteristics of orthorhombic martensite (α″) formed by step-quenching in a Ti-30Nb-4Sn (wt%) alloy have been investigated by transmission electron microscopy (TEM) and X-ray diffraction (XRD). According to literature, α″ lattice parameters depend mainly on the composition of the parent β phase. In this study, samples subjected to step quenching heat treatment presented α″ phase formation in the proximity of α phase laths, driven by two combined factors: solute rejection and lattice strain. Our results indicate that as the aging is prolonged, α″ becomes richer in solute content, which makes it more similar to the parent β phase. An average 2.55% lattice strain along β directions was found to be necessary in order to obtain α″ from the β phase after 24 h of aging at 400 °C, followed by water-quenching. The initial lattice strain along the same direction was estimated at approximately 3.60% with zero aging time. The precipitation of the α phase does not inhibit a solute rich α″ phase formation|
|Appears in Collections:||FEM - Artigos e Outros Documentos|
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.