Title: Influence of Si substitution on the reactivity of α-tricalcium phosphate
Author: Motisuke, Mariana
Mestres, Gemma
Renó, Caroline O.
Carrodeguas, Raúl G.
Zavaglia, Cecília A.C.
Ginebra, Maria-Pau
Abstract: Silicon substituted calcium phosphates have been widely studied over the last ten years due to their enhanced osteogenic properties. Notwithstanding, the role of silicon on α-TCP reactivity is not clear yet. Therefore, the aim of this work was to evaluate the reactivity and the properties of Si-α-TCP in comparison to α-TCP. Precursor powders have similar properties regarding purity, particle size distribution and specific surface area, which allowed a better comparison of the Si effects on their reactivity and cements properties. Both Si-α-TCP and α-TCP hydrolyzed to a calcium-deficient hydroxyapatite when mixed with water but their conversion rates were different. Si-α-TCP exhibited a slower setting rate than α-TCP, i.e. kSSA for Si-TCP (0.021 g·m− 2·h− 1) was almost four times lower than for α-TCP (0.072 g·m− 2·h− 1). On the other hand, the compressive strength of the CPC resulting from fully reacted Si-α-TCP was significantly higher (12.80 ± 0.38 MPa) than that of α-TCP (11.44 ± 0.54 MPa), due to the smaller size of the entangled precipitated apatite crystals
Subject: Cimento
Country: Países Baixos
Editor: Elsevier
Rights: Fechado
Identifier DOI: 10.1016/j.msec.2017.02.099
Address: https://www.sciencedirect.com/science/article/pii/S0928493116321300
Date Issue: 2017
Appears in Collections:FEM - Artigos e Outros Documentos

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.