Title: Desempenho "in vitro" de adesivos condiciona-e-lava de 2 passos modificado por aditivos de tiouretano : "In vitro" performance of 2-step, total etch adhesives modified by thiourethane additives
Title Alternative: "In vitro" performance of 2-step, total etch adhesives modified by thiourethane additives
Author: Puppin-Rontani, Julia, 1990-
Advisor: Correr Sobrinho, Lourenço, 1960-
Abstract: Resumo: Objetivo: avaliar as propriedades físicas e a resitência de união à microtração de adesivos experimentais contendo oligômeros de tiouretano (TU) e/ou partículas de carga funcionalizadas com TU. Materiais e métodos: uma matriz orgânica base contendo 60%BisGMA/40%HEMA (peso) +0,2% DMPA 1 (fotoiniciador) + 0,5% BHT(inbidor) - (BH-controle) foi formulada; o oligômero de TU PETMP-DEMODUR (tetrafuncional) foi sintetizado e adicionado em 20%(peso) à matriz orgânica dos grupos contendo TU (BH+ 20%TU); para os grupos contendo partículas de carga, estas foram funcionalizadas com metacrilato-MF ou com tiouretano-TF e adicionadas em 10%(vol). Os grupos experimentais foram: BH; BH+10%MF; BH+10%TF; BH+20%TU+10%MF; BH+20%TU+10%TF; BH+20%TU. Os grupos foram submetidos aos testes: resistência de união à microtração (RUMT) em 24 h e 6 meses em dentina hígida (n=6); resistência à flexão (RF) por três pontos em ambiente seco (n=6) e armazenadas em água por 7 dias (n=6); Cinética de polimerização (n=3) (grau de conversão-GC e taxa máxima de polimerização-Rpmax); Sorção e Solubilidade (SR/SL) (n=3); e, Viscosidade (V)(n=3). Para a RUMT, foi adicionado 40% etanol(vol) aos grupos experimentais. Os dados foram submetidos a ANOVA um fator e teste de Tukey (p<0,05). Para a comparação entre os tempos de armazenagem das amostras da RUMT, foi aplicado o test (p<0,05). Para a RUMT (p=0,13) e SR/SL (p>0,5) e RF a seco (p>0,05), não houve diferença significativa entre os grupos. Os grupos contendo TU na matriz apresentaram os menores valores de RF (p<0,05) quando armazenados por 7 dias em água. Os grupos contendo TU na matriz apresentaram os maiores valores de GC e não houve diferença significativa entre os grupos quanto a GC-na-Rpmax. A Rpmax foi maior para o BH+20%TU+10%MF, seguido pelo BH e BH+10%TF, e os menores valores encontrados para os BH+10%MF, BH+20%TU+10%TF e BH+20%TU. Os grupos contendo TU na matriz mostraram maiores valores de viscosidade, sendo o BH+20%TU+10%TF, o qual possui TU na matriz e na funcionalização das cargas, o maior valor de viscosidade. Conclusão: Tendo em vista que a adição de TU na matriz melhorou o grau de conversão final, conclui-se que a adição de TU na matriz de adesivos experimentais apresenta-se como uma estratégia promissora

Abstract: The aim of the study was to evaluate the effect of adding thio-urethane oligomers (TU) on physical properties and the microtensile bond strength of experimental adhesive and/or thio-urethane functionalized fillers. One organic base-matrix was formulated containing BisGMA/HEMA (60%/40%wt) (BH) + 0.2% DMPA 1 (photoinitiator) + 0.5% BHT(inhibitor) ¿ BH (control); the thio-urethane oligomer was added in 20%(wt) for the groups containing TU in the matrix; and for the groups containing fillers, fillers were functionalized with methacrylate (MF) or thio-urethane (TF) and added in 10%(wt). The experimental adhesives groups were: BH; BH+10%MF; BH+10%TF; BH+20%TU+10%MF; BH+20%TU+10%TF; BH+20%TU. For the mechanical properties, the experimental groups were submitted to Microtensile bond strength (n=6) (24h and 6 months), Yield Strength (YS) and Modulus (YM) (n=6) (wet and dry), Polymerization kinects (n=3) (final degree of conversion-DC and maximum tax of polymerization-Rpmax), Water Sorption/Solubility (WS/SL) (n=3) and Viscosity (n=3). For the microtensile bond strength test 40% ethanol (vol) was added to the experimental groups and 36 molars were selected and divided in 6 groups (n=6) that were analyzed in 24h and 6 months of storage in water. The data were submitted to one-way ANOVA and Tukey post-hoc test (p>0.05). For the comparison of storage time for the microtensile bond strength test, data were submitted to t test (p>0.05). For the microtensile bond strength test (p=0.13) and WS/SL (p>0.05), no significant difference was found between groups. For the YS and YM (p>0.05), the dry evaluation had no significant difference in YS, although for the YM BH+10%MF, BH+10%TF and BH+20%TU+10%MF had the highest values compared to BH, BH+20%TU+10%TF and BH+20%TU and in the wet evaluation, the groups containing TU in the matrix had the lowest values in YS and YM. The polymerization kinects for the groups containing TU in the matrix had the highest DC and no significant difference was found between groups for the DC at Rpmax. The Rpmax was higher for the BH+20%TU+10%MF, followed by BH and BH+10%TF, and the lowest Rpmax values were found for the BH+10%MF, BH+20%TU+10%TF and BH+20%TU. The groups containing TU in the matrix had the highest values for viscosity, being that the BH+20%TU+10%TF that has TU in the matrix and on the functionalized fillers had the highest values with statistical significant difference for the BH+20%TU+10%MF and BH+20%TU. The addition of TU in the matrix improved the final degree of conversion of the experimental adhesives and the bond strength maintained stable after 6 months of storage in water. With that, the addition of TU in the matrix of experimental adhesives improved the final Degree of conversion is a promising strategy
Subject: Adesivos dentinários
Materiais dentários
Resistência à tração
Language: Multilíngua
Editor: [s.n.]
Citation: PUPPIN-RONTANI, Julia. Desempenho "in vitro" de adesivos condiciona-e-lava de 2 passos modificado por aditivos de tiouretano: "In vitro" performance of 2-step, total etch adhesives modified by thiourethane additives. 2020. 1 recurso online (53 p.) Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP.
Date Issue: 2020
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Puppin-Rontani_Julia_D.pdf1.31 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.