Please use this identifier to cite or link to this item: http://repositorio.unicamp.br/jspui/handle/REPOSIP/344885
Type: Artigo
Title: Self-organized lead(II) sulfide quantum dots superlattice
Author: Silva Filho, José Maria C. da
Ermakov, Victor A.
Bonato, Luiz G.
Nogueira, Ana F.
Marques, Francisco C.
Abstract: We show that superlattice (SL) of PbS quantum dots (QD) can be easily prepared by drop casting of colloidal QD solution onto glass substrate and the ordering level can be controlled by the substrate temperature. A QD solution was dropped on glass and dried at 25, 40, 70 and 100 degrees C resulting in formation of different SL structures. X-ray diffractograms (XRD) of deposited films show a set of sharp and intense peaks that are higher order satellites of a unique peak at 1.8 degrees (two theta), which corresponds, using the Bragg's Law, to an interplanar spacing of 5.3 nm. The mean particles diameter, calculated through the broadening of the (111) peak of PbS using the Scherrer's formula, were in agreement with the interplanar spacing. Transmission electron microscopy (TEM) measurements were also used to study the SL structure, which showed mainly a face centered cubic (FCC) arrangement of the QD. The photoluminescence (PL) spectrum of QD in the SL showed a shift toward lower energy compared to one in solution. It can be attributed to the fluorescence resonant energy transfer (FRET) between neighbors QD's. Moreover, we observed greater redshift of PL peak for film with lower drying temperature, suggesting that it has a more organized structure.
Subject: Automontagem (Química)
Semicondutores
Raios X - Difração
Self-assembly (Chemistry)
Semiconductors
X-rays - Diffraction
Country: Estados Unidos
Editor: Cambridge University Press
Rights: fechado
Identifier DOI: 10.1557/adv.2017.246
Address: https://www.cambridge.org/core/journals/mrs-advances/article/selforganized-leadii-sulfide-quantum-dots-superlattice/043784604F64CA7833E348B67B9759C8
Date Issue: 2017
Appears in Collections:IQ - Artigos e Outros Documentos
IFGW - Artigos e Outros Documentos

Files in This Item:
File SizeFormat 
000412731500004.pdf499.87 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.