Title: Hydrogen storage properties of filings of the ZK60 alloy modified with 2.5 wt% mischmetalHydrogen storage properties of filings of the ZK60 alloy modified with 2.5 wt% mischmetal
Author: Silva, E.P.
Leiva, D.R.
Floriano, R.
Oliveira, V.B.
Pinto, H.C.
Botta, W.J.
Abstract: In this study, a commercial Mg-based ZK60 alloy was modified with 2.5 wt% mischmetal (ZK60-2.5 wt%Mm) and further processed by cold rolling followed by manual filing. The chips obtained by manual filing process were collected from the as cast (AC) and the cold rolled (CR) materials. The hydrogen storage properties were evaluated by kinetics measurements at 350 °C. A full microstructural characterization including optical, scanning and transmission electron microscopy (MO, MEV and TEM), X-ray diffraction (XRD) and differential scanning calorimetry (DSC) was performed in the samples. For the first absorption of both filed samples the H storage capacity showed a value around 6.0 wt% after 1 h while for the CR sample it was close to 1.25 wt% after the same time. The manual filing produced samples with higher hydrogenation kinetics compared with that of the CR sample. Besides, their hydrogen storage capacity was maintained close to the theoretical value (6.75 wt%). The breakage and pulverization of the intermetallic phases gave the chips from the CR alloy the faster hydrogenation kinetics, especially for H-desorption
Subject: Hidrogênio
Country: Reino Unido
Editor: Elsevier
Rights: Fechado
Identifier DOI: 10.1016/j.ijhydene.2019.05.207
Address: https://www.sciencedirect.com/science/article/abs/pii/S0360319919321226
Date Issue: 2020
Appears in Collections:FCA - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
2-s2.0-85068057455.pdf3.3 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.