Title: Bond strength of CAD/CAM restorative materials treated with different surface etching protocols
Author: Colombo, Lucas do Amaral
Murillo-Gomez, Fabian
De Goes, Mario Fernando
Abstract: Purpose: To evaluate the effect of different surface treatments on the surface morphology of CAD/CAM ceramics and on their bond strength to cement. Materials and Methods: Sixty cubic sections were cut from each of three materials (lithium disilicate glass-ceramic [DL], leucite-based glass-ceramic [LC], resin-matrix ceramic composite [RMCC]) and were treated as follows (n = 10): 1. no treatment (C); 2. 5% hydrofluoric acid applied for 20 s plus silane (HF5% 20 s); 3. 5% hydrofluoric acid applied for 60 s plus silane (HF5% 60 s); 4. 10% hydrofluoric acid applied for 20 s plus silane (HF10% 20 s); 5. 10% hydrofluoric acid applied for 60 s plus silane (HF10% 60 s); 6. Self-etching ceramic primer (MBEP). Ceramic cubes were bonded to pre-polymerized composite resin cubes with a composite cement. Each set was cut into stick-shaped specimens (1 +/- 0.3 mm(2)). After 24-h water storage, microtensile bond strength (mu TBS) was measured. Data were analyzed using two-way ANOVA and Tukey's test (alpha = 0.05). Failure pattern and surface morphology were assessed using scanning electron microscopy (SEM). Results: Both factors significantly influenced mu TBS, while no interaction between factors was found. RMCC presented statistically higher mu TBS values than LC and DL, while the surface treatments HF5% 20 s, HF5% 60 s, HF10% 20 s, HF10% 60 s and MBEP, did not show statistical differences between them, although they resulted in statistically significantly higher bond strengths than did C groups. A high number of pre-test failures were detected in the control groups for all materials. MBEP produced less extensive surface alterations than did all HF treatments. Conclusion: All of the hydrofluoric acid treatments tested showed similar cement-ceramic bonding efficacy. The self-etching ceramic primer produced less surface alterations and comparable bonding efficacy compared to separate hydrofluoric acid/silane primer application.
Subject: Acido fluoridrico
Resistência de união
Country: Reino Unido
Editor: Quintessence Publishing
Rights: Fechado
Identifier DOI: 10.3290/j.jad.a42931
Address: https://jad.quintessenz.de/index.php?doc=abstract&abstractID=42931/
Date Issue: 2019
Appears in Collections:FOP - Artigos e Outros Documentos

Files in This Item:
File Description SizeFormat 
000483937700003.pdf1.38 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.