Title: Análise-físico química de um compósito resinoso experimental contendo como co-iniciador tris (trimetilsilil) silano : Chemical physical properties of experimental resin based composite with tris (trimethylsilyl) silano
Title Alternative: Chemical physical properties of experimental resin based composite with tris (trimethylsilyl) silano
Author: Nobre, Caio Felipe de Almeida, 1995-
Advisor: Sinhoreti, Mário Alexandre Coelho, 1969-
Abstract: Resumo: O objetivo no presente estudo foi avaliar as propriedades físico-químicas de um compósito resinoso utilizando Tris (trimetilsilil) silano (TTMSS) como co-iniciador. Foram confeccionados seis compósitos experimentais contendo 35% em peso de matriz orgânica (10,2% em peso de BisGMA, 11,1% em peso de BisEMA10 e UDMA e 2,1% em peso de TEGDMA) e 65% de carga (13% em peso de sílica e 52% em peso de BaBSiO2). Assim os 6 grupos foram:TD0.5 (0,2% CQ/ 0,5% TTMSS/ 0,5% DPIHP); TD1 (0,2% CQ/ 1% TTMSS/ 0,5% DPIHP); DTD (0,2% CQ/ 0,25% TTMSS/ 0,25% DMAEMA/ 0,5% DPIHP); DT (0,2% - CQ/ 0,25% -TTMSS/ 0,25% DMAEMA); T0.5 (0,2% - CQ/ 0,5% -TTMSS); C (0,2% - CQ/ 0,5% -DMAEMA). Os testes de Grau de Conversão e Taxa de Polimerização foram realizados por espectroscopia Micro Raman (n=5). Para o teste de alteração de cor foram utilizadas amostras em forma de disco (10 mm x 1 mm; n = 5) submetidas a envelhecimento por luz UV, onde ?E00 de cada amostra foi calculado pela fórmula CIEDE2000. A profundidade de cura por dureza Knoop foi realizada em profundidades de 200 ?m, 1 mm, 2 mm e 3 mm da superfície superior a inferior das amostras (n=5). Amostras em forma de barra (10 mm x 2 mm x 2 mm) (n = 10) foram confeccionadas e submetidas ao teste de flexão de três pontos. O teste de Tensão de Contração foi realizado utilizando-se máquina de ensaio universal. Barras de vidro (diâmetro de 4 mm; comprimento de 13 e 54 mm) foram fixadas e alinhadas, deixando 1mm de espaço entre as superfícies onde os compósitos experimentais foram polimerizados. Com os resultados foi possível verificar que TTMSS a 0,5 % reduziu a taxa de conversão, resultando em menor contração de polimerização sem reduzir as propriedades mecânicas dos compósitos experimentais. A associação de DMAEMA com TTMSS formou radicais que reduziram a eficiência da polimerização e a substituição de DMAEMA não alterou a cor dos compósitos experimentais. Dessa forma, foi possível concluir que a substituição de DMAEMA por TTMSS possibilitou a redução das tensões de contração de polimerização. A associação dos co-iniciadores em um compósito reduziu a eficiência da polimerização. Além disso, a utilização de TTMSS não alterou a cor dos compósitos experimentais

Abstract: The purpose of this study was to evaluate the incorporation of Tris (trimethylsilyl) silane (TTMSS) as co-initiator in the resin-based composite. Six RBC were made containing 35 wt% of organic matrix (10.2 wt% BisGMA, 11.1 wt% BisEMA10 and UDMA and 2.1 wt% TEGDMA) and 65% filler (13 wt% fumed silica and 52 wt% BaBSiO2). The 6 groups were: TD0.5 (0.2 wt% CQ/ 0.5 wt% TTMSS/ 0.5 wt% DPIHP); TD1 (0.2 wt% CQ/ 1 wt% TTMSS/ 0.5 wt% DPIHP); DTD (0.2 wt% CQ/ 0.25 wt% TTMSS/ 0.25 wt% DMAEMA/ 0.5 wt% DPIHP); DT (0.2 wt% - CQ/ 0.25 wt% -TTMSS/ 0.25 wt% DMAEMA); T0.5 (0.2 wt% - CQ/ 0.5 wt% -TTMSS); C (0.2 wt% - CQ/ 0.5 wt% -DMAEMA). Degree of Conversion and Rate of Polymerization tests were performed by Micro-Raman spectroscopy (n=5). The polymerization rate was used the same parameter and the blends were scanned 14 times for 40s. For the Color Change Analysis test, disc-shaped specimens (10 mm in diameter and 1 mm thick; n=5) were used. The specimens were UV-light aged and ?E00 of each specimen was calculated using a spectrophotometer with the CIEDE2000 formula. Depth of Cure by Knoop hardness were performed on depths of 200 ?m, 1 mm, 2 mm and 3 mm from the top to bottom surface of each specimen (semicircular: 3 mm in depth and 4 mm in internal diameter; n=5). Bar-shaped specimens (10 mm x 2 mm x 2 mm) (n=10) were made to Flexural Strength and Flexural Modulus submitted to three-point bending test using a universal testing machine. Polymerization Shrinkage Stress was analyzed using the universal testing machine method. Glass rods (diameter, 4 mm; 13 and 54 mm in length) were aligned, leaving a vertical gap of 1 mm between the rods and the composites between them were light-cured. A video extensometer was placed perpendicular to the gap in order to calculate the strain (in ?m) between the two rods. As the results it was possible to observe that the use of 0.5 wt% TTMSS decrease Rate of Polymerization and Polymerization Shrinkage Stress, without reducing the mechanical properties of the RBC. The amine radicals of DMAEMA can react with TTMSS reducing the maximum polymerization rate and RCB with TTMSS were not decrease the color change. According to the results, it was possible to conclude that replacing DMAEMA with TTMSS enabled a reduction in PSS. However, combining between TTMSS and DMAEMA reduced the Rp and the RBC with TTMSS did not reduce the yellowing effect
Subject: Resinas compostas
Fotoiniciadores dentários
Pigmentação
Cor
Polimerização
Estabilidade
Language: Português
Editor: [s.n.]
Citation: NOBRE, Caio Felipe de Almeida. Análise-físico química de um compósito resinoso experimental contendo como co-iniciador tris (trimetilsilil) silano: Chemical physical properties of experimental resin based composite with tris (trimethylsilyl) silano. 2020. 1 recurso online (33 p.) Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: http://www.repositorio.unicamp.br/handle/REPOSIP/339989. Acesso em: 30 Apr. 2020.
Date Issue: 2020
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Nobre_CaioFelipeDeAlmeida_M.pdf1.08 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.