Title: Propriedades mecânicas residuais do concreto em situação de incêndio
Title Alternative: Residual mechanical properties of the concrete in fire conditions
Author: Sollero, Marcela Barros de Souza, 1987-
Advisor: Moreno Junior, Armando Lopes, 1964-
Abstract: Resumo: A norma ABNT NBR 15200:2012 determina que as estruturas de concreto sejam projetadas para resistir aos efeitos das altas temperaturas por um determinado tempo e que as estruturas incendiadas sejam vistoriadas e tenham sua capacidade portante verificada antes de sua reutilização. Tanto o projeto quanto a verificação das estruturas baseiam-se na correlação entre o comportamento dos materiais em temperatura ambiente e em situação de incêndio. A normatização atual, no entanto, apresenta lacunas tanto em relação ao comportamento em situação de incêndio de concretos executados com diferentes tipos de agregados graúdos, característica que afeta marcantemente seu desempenho, quanto às condições de ensaio para a avaliação da resistência mecânica residual do material. A pesquisa desenvolvida objetiva fornecer subsídio para o dimensionamento e a verificação de estruturas de concreto em situação de incêndio. Para isso, foi realizado um Programa Experimental dedicado à obtenção de curvas de decréscimo da resistência mecânica residual de amostras de concreto executadas com granito, basalto e calcário e expostas a temperaturas compreendidas entre 100ºC e 900ºC, de resistência normal e alta, fundamentando-se nas recomendações RILEM TC 200-HTC e RILEM TC 129-MHT. Os resultados de resistência à compressão obtidos apresentaram-se semelhantes ou superiores aos valores de resistência residual de referência nas temperaturas mais baixas; uma vez superadas, parte dos valores de referência se mostraram contra a segurança. Constatou-se ainda, através de análise estatística, a influência do tipo de agregado graúdo utilizado e o desempenho estatisticamente equivalente da sílica ativa e da sílica de casca de arroz, assim como a possibilidade de se reduzir o tempo de latência das amostras através de pré-aquecimento do concreto. Por fim, evidenciou-se a necessidade de revisão das principais normas vigentes relacionadas ao projeto de estruturas em situação de incêndio, de forma a incluir dados de propriedades mecânicas residuais de concreto de resistência à compressão normal e alta com diferentes tipos de agregados graúdos

Abstract: ABNT NBR 15200:2012 standard determines that concrete structures must be designed to resist high-temperature effects for a specified time and that structures that have been through fire situations must be inspected and have its bearing capacity verified before its reuse. Both the project and the verifying process are based on the correlation between the room temperature and the fire situation behavior of the materials. However, there are gaps in current standards relating to the behavior in fire situations of concrete made with different types of coarse aggregate, which greatly affects its performance, and also relating to the testing conditions for the residual mechanical properties of the materials. The developed research aims to provide a subsidy for dimensioning and verification of concrete structures in fire situation. To this end, it was developed an Experimental Program focused on obtaining residual mechanical properties reduction curves of concrete samples produced with granite, basalt, and limestone coarse aggregate and exposed to a range of temperatures between 100ºC and 900ºC, based on RILEM TC 200-HTC and RILEM TC 129-MHT recommendations. The achieved compressive strength results were similar or superior to the reference residual strength values in lower temperatures, once over them part of the reference values were revealed against safety. Through statistical analysis, it was verified the influence of the coarse aggregate type and that silica fume and rice husk ash are statistically equivalent in performance, it was also found that the latency time for samples can be reduced pre-heating the concrete. Lastly, the necessity to revise the main standards related to fire-exposed structure design was shown, there is a need to include data on the residual mechanical properties of normal and high strength concrete made with different types of coarse aggregates
Subject: Concreto - Propriedades mecânicas
Fogo
Altas temperaturas
Agregados (Materiais de construção)
Language: Português
Editor: [s.n.]
Citation: SOLLERO, Marcela Barros de Souza. Propriedades mecânicas residuais do concreto em situação de incêndio. 2019. 1 recurso online (215 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil, Arquitetura e Urbanismo, Campinas, SP. Disponível em: http://www.repositorio.unicamp.br/handle/REPOSIP/336163. Acesso em: 19 mar. 2020.
Date Issue: 2019
Appears in Collections:FEC - Tese e Dissertação

Files in This Item:
File SizeFormat 
Sollero_MarcelaBarrosDeSouza_M.pdf9.11 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.