Abstract: Resumo: A remineralização de dentina é de considerável interesse clínico para a Hipersensibilidade Dentinária e o desenvolvimento de análogos biomiméticos capazes de regular a nucleação e o crescimento da hidroxiapatita (HAp) ainda é um desafio. O objetivo deste trabalho foi avaliar in vitro o potencial de remineralização dentinária utilizando os seguintes poli-catecóis: Polidopamina, Poli-DOPA, Poli-Ácido Cafeico e o peptídeo DOPA-RP ((DOPA-Ahx-(Gly)3-(Glu)5) contendo tanto domínio de ligação ao colágeno como ao cálcio que foi sintetizado por química em fase sólida. Amostras de dentina foram obtidas de terceiros molares humanos e condicionadas com ácido fosfórico 37% por 2 minutos para desmineralização. Em seguida, foram divididas aleatoriamente em 4 grupos experimentais (n=10) e imersas em solução tampão fosfato (PBS) (pH 6) recém preparada contendo 1mg/ 10mL do respectivo análogo biomimético e 1mg/ 10mL de Lacase mantida por 12 h em estufa a 37 °C. Após o tratamento biomimético, as amostras foram imersas em 10 ml de solução remineralizadora a 37 °C e a solução foi trocada todos os dias por 10 dias. Amostras de dentina intacta e desmineralizadas foram utilizadas como grupos controle (n = 10) e mantidas em água deionizada nas mesmas condições que os grupos experimentais. A dentina remineralizada foi caracterizada por microscopia eletrônica de varredura (MEV), espectroscopia de raios X por dispersão de energia (?EDX) e difração de raios-X (DRX). A aplicação de diferentes poli-catecóis e do peptídeo DOPA-RP promoveu a nucleação de cristais e a formação de HAp, similar à dentina biológica intacta, tanto na superfície dentinária como nas paredes dos túbulos dentinários. Ao imitar o papel das proteínas não-colagenosas carregadas in vivo, os polímeros consistindo de grupos catecol mostraram a capacidade de modificar as propriedades da superfície da dentina desmineralizada, promovendo a formação de minerais. O uso de poli-catecóis pode ser, portanto, incentivado para o desenvolvimento de uma técnica terapêutica para hipersensibilidade dentinária

Abstract: Remineralization of dentin is of considerable clinical interest for Dentin Hypersensitivity and the development of biomimetic analogs able to regulate hydroxyapatite (HAp) nucleation and growth is still a challenge. This study aimed to evaluate in vitro the potential for dentin remineralization using the following prepared poly(catechols): poly(dopamine), poly(DOPA), poly(caffeic acid) and the peptide DOPA-RP ((DOPA-Ahx-(Gly)3-(Glu)5) containing both collagen and calcium-binding domains, which was synthesized by solid-phase chemistry. Dentin samples were prepared from sound human molars and etched with 37% of phosphoric acid for 2 minutes. The samples were randomly divided into 4 experimental groups (n = 10) and immersed in a 1mg/ 10mL freshly prepared solution of the respective biomimetic analog on phosphate buffer solution (PBS) (pH 6) with 1mg/ 10mL of Laccase for 12 h at 37 °C. After the treatment reaction, they were immersed in 10mL of the calcium and phosphate remineralization solution at 37 °C and the solution was changed every day for 10 days. Samples of intact and demineralized dentin were used as control groups (n = 10) and kept in deionized water under the same conditions of the experimental ones. The remineralized dentin was characterized by scanning electron microscopy (SEM), energy dispersion X-ray spectroscopy (?EDX) and X-ray diffraction (DRX). The application of different poly(catechols) and DOPA-peptide promoted crystal nucleation and the formation of HAp similar to biological intact dentin, which covered both the dentin surface and dentinal tubules walls. By mimicking the role of charged non-collagenous proteins in vivo, polymers consisting of catechol groups showed the ability to modify demineralized dentin surface properties, promoting mineral formation. The use of poly(catechols) may be encouraged for the development of a therapeutic technique for dentin hypersensitivity
Subject: Remineralização dentária
Colágeno
Hidroxiapatita
Sensibilidade da dentina
Language: Inglês
Editor: [s.n.]
Citation: LIMA, Joyce Figueiredo Macedo de. Efeito de materiais biomiméticos na remineralização dentinária: Effect of biomimetic materials on dentin remineralization. 2019. 1 recurso online (57 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP.
Date Issue: 2019
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Lima_JoyceFigueiredoMacedoDe_M.pdf8.33 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.