Title: Efeitos da radiação gama e do fluoreto sobre dentes decíduos : estudos in vitro = Effects of gamma radiation and fluoride on primary teeth: in vitro studies
Title Alternative: Effects of gamma radiation and fluoride on primary teeth : in vitro studies
Author: Lopes, Lenita Marangoni, 1989-
Advisor: Nobre dos Santos, Marinês, 1956-
Abstract: Resumo: OBJETIVO: Avaliar se a radioterapia por radiação gama causa mudanças na composição mineral e orgânica, microdureza e morfologia do esmalte e da dentina dos dentes decíduos; na susceptibilidade dos dentes decíduos irradiados ao desafio cariogênico; e se a associação de dentifrício fluoretado e aplicação tópica de flúor fosfato acidulado (FFA) inibe a perda mineral do esmalte decíduo irradiado. MATERIAL E MÉTODOS: No artigo I, os espécimes de esmalte e a dentina de dentes decíduos (n=30) foram submetidos à microdureza superficial, composição (Raman) e microscopia eletrônica de varredura (MEV) antes, e ao atingir as doses de 1080, 2160 e 3060 cGy de radiação. No artigo II, foi utilizado um modelo biológico para avaliar a susceptibilidade do esmalte decíduo irradiado ao desafio cariogênico (n=18). A profundidade, área e volume da lesão da cárie foram avaliados por microtomografia computadorizada e MEV. No artigo III, espécimes foram randomizados em oito grupos (n=13): Não irradiado + Dentifrício não fluoretado (DNF) (G1); Não irradiado + Dentifrício fluoretado (DF ¿ 1100 ppm) (G2); Não irradiado + DNF + FFA (G3), Não irradiado + DF + FFA (G4); Irradiado + DNF (G5); Irradiado + DF (G6); Irradiado + DNF + FFA (G7); Irradiado + DF + FFA (G8). Todos os grupos foram submetidos a ciclagem de pH e ao respectivo dentifrício duas vezes ao dia. Foi realizada microdureza transversal e microscopia de luz polarizada. RESULTADOS: Os resultados do artigo I mostraram que a microdureza da superfície do esmalte diminuiu ao atingir a dose de 2160 cGy. Para a dentina, a microdureza da superfície diminuiu ao atingir 1080 cGy e 2160 cGy. O conteúdo mineral de fosfato, carbonato, amida e hidrocarbonetos do esmalte diminuiu ao atingir 3060 cGy. Para a dentina, observamos um aumento crescente do conteúdo de fosfato v1, amida e hidrocarbonetos ao atingir as doses de 1080 e 2160 cGy e uma redução ao atingir 3060 cGy. As imagens por MEV mostraram trincas no esmalte e a degradação da dentina peri-tubular. No artigo II, observou-se que a profundidade e a área da lesão no grupo irradiado foram significativamente maiores do que no grupo não irradiado. No entanto, o volume da lesão não diferiu entre os grupos. As imagens por MEV mostram perda de estrutura do esmalte no grupo irradiado. No artigo III, os grupos G1 e G3 apresentaram perda mineral estatisticamente maior do que G2 e G4. Não foi encontrada diferença estatística entre os grupos irradiados. As imagens por microscopia de luz polarizada mostraram maior birrefringência positiva nos grupos G5, G6, G7 e G8, e presença da linha de remineralização nos grupos G2, G3, G4 e G6. CONCLUSÃO: A radioterapia usando radiação gama causou redução da microdureza da superfície, alteração da composição mineral e orgânica e alterações morfológicas no esmalte e na dentina dos dentes decíduos. Essas mudanças tornaram os dentes decíduos irradiados mais susceptíveis ao desafio cariogênico e o uso de dentifrício fluoretado e FFA não teve sua efetividade detectada na redução da perda mineral de dentes decíduos irradiados

Abstract: AIM: To evaluate whether the radiotherapy with gamma radiation causes changes on the mineral and organic composition, microhardness, and morphology of enamel and dentin of primary teeth; the susceptibility of primary teeth to a cariogenic challenge; and if the association of fluoride dentifrice and topical application of fluoride reduces the mineral loss of irradiated primary enamel. MATERIAL AND METHODS: In Article I, specimens of primary enamel and dentin (n=30) were submitted to surface microhardness, composition, and scanning electron microscopy (SEM) analyses before, at 1080, 2160, and 3060 cGy of gamma radiation. In Article II, a biological model was used to evaluate the susceptibility of the irradiated primary enamel (n=18) to the cariogenic challenge. The depth, area, and volume of the caries lesion were evaluated by microcomputer tomography, and a qualitative analysis was performed using SEM analysis. In Article III, 104 specimens of primary enamel were randomized into eight treatment groups (n=13): Non-irradiated + Non-fluoride dentifrice (NFD) (G1); Non-irradiated + Fluoride dentifrice (FD ¿ 1100 ppm) (G2); Non-irradiated + Acidulated phosphate fluoride (APF-gel) + NFD (G3), Non-irradiated + APF-gel + FD(G4); Irradiated + NFD (G5); Irradiated + FD (G6); Irradiated + APF-gel + NFD (G7); Irradiated + APF-gel + FD (G8). All groups were submitted to a pH cycling with the respective dentifrice twice daily. Specimens were submitted to transverse microhardness analysis and polarized light microscopy (PLM) analysis. RESULTS: The results of Article I showed that microhardness of the enamel surface decreased at 2160 cGy of radiation. For dentin, the surface microhardness decreased at 1080 cGy and 2160 cGy doses. The phosphate, carbonate, amide III, and hydrocarbons contents of enamel, decreased at 3060 cGy. For dentin, we noticed a growing increase in phosphate v2, amide III and hydrocarbons content at 1080 and 2160 cGy and a reduction at 3060 cGy. SEM images showed a cracked aspect on enamel surface, and degradation of peri-tubular dentin. In Article II, it was observed that the lesion depth and area of caries lesion in the irradiated group were significantly higher than in the non-irradiated group. However, the lesion volume did not differ among the groups. The SEM images showed enamel breakdown in irradiated group. In Article III, G1 and G3 groups showed statistically higher mineral loss than G2 and G4 groups. The reduction of mineral loss provided by fluoride dentifrice, APF application as well as by their combination, did not differ from control group. The PLM images show a higher positive birefringence in the groups G5, G6, G7, and G8, and the presence of a surface layer of remineralizarion in groups G2, G3, G4 and G6. CONCLUSION: Radiotherapy with gamma radiation reduced surface microhardness, changed mineral and organic composition, and promoted morphological changes on the enamel and dentin surface of primary teeth. These changes turned irradiated primary teeth more susceptible to a cariogenic challenge. In addition, the effectiveness of fluoride dentifrice and APF-gel in reducing the mineral loss of gamma irradiated primary teeth could not be demonstrated
Subject: Dentes deciduos
Cárie dentária
Radioterapia
Language: Português
Editor: [s.n.]
Citation: LOPES, Lenita Marangoni. Efeitos da radiação gama e do fluoreto sobre dentes decíduos: estudos in vitro = Effects of gamma radiation and fluoride on primary teeth: in vitro studies. 2018. 1 recurso online (66 p.). Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP.
Date Issue: 2018
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Lopes_LenitaMarangoni_D.pdf1.62 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.