Title: Caracterização comparativa entre os aços inoxidáveis austeníticos para implantes cirúrgicos ASTM F138 comercial e obtido por manufatura aditiva DMLS
Title Alternative: Comparative characterization surgical austenitic stainless steel ASTM F138 and additive manufactured powder bed laser fused austenitic stainless steel
Author: Busato Junior, Edgar, 1957-
Advisor: Zavaglia, Cecília Amélia de Carvalho, 1954-
Abstract: Resumo: A manufatura aditiva é um processo recente que possibilita a confecção de peças com geometrias consideradas complexas para os métodos de fabricação convencionais. A possibilidade de obtenção de peças em aço inoxidável austenítico pela técnica de Sinterização Direta de Metal por Laser (DMLS) torna o processo de manufatura aditiva ideal para fabricação de implantes cirúrgicos personalizados. O pó comercial EOS 316L, produzido pela EOS GmbH, utilizado na produção das amostras estudadas nesse trabalho, apresenta composição química equivalente ao do aço inoxidável austenítico tipo cirúrgico ASTM F138. As amostras produzidas foram submetidas a diferentes tratamentos térmicos tendo posteriormente sido submetidas à caracterização mecânica e microestrutural por meio de microscopia de luz visível, microscopia eletrônica de varredura, espectroscopia de energia dispersiva - EDS, e difração de raios-X. Ensaios de microdureza Vickers foram realizados nas mesmas, e suas resistências ao desgaste microabrasivos avaliadas. Os resultados obtidos para o material produzido por DMLS foram comparados aos do aço ASTM F138 comercial e mostram que o material produzido por manufatura aditiva apresenta características similares ao aço inoxidável para uso cirúrgico

Abstract: Additive Manufacturing is a recent process that enables the fabrication of products with geometries that are considered complex for conventional manufacturing methods. The possibility of obtaining parts in austenitic stainless steel by the technique of Direct Metal Laser Sintering (DMLS) makes the Additive Manufacturing process ideal for the manufacture of customized surgical implants. The EOS 316L commercial powder, produced by EOS GmbH, used in the production of the samples studied in this work, presents a chemical composition equivalent to that of austenitic stainless steel type ASTM F138. The samples were submitted to different thermal treatments and then subjected to mechanical and microstructural characterization by means of visible light microscopy, scanning electron microscopy, EDS, and X-ray diffraction. Vickers microhardness tests were performed on them, and their microabrasive wear resistance was evaluated. The results obtained for the material produced by DMLS were compared to those of the ASTM F138 commercial steel and show that the material produced by additive manufacture presents characteristics similar to stainless steel for surgical use
Subject: Prototipagem rápida
Aço inoxidável austenítico
Próteses e implantes
Biomateriais
Caracterização de materiais
Language: Português
Editor: [s.n.]
Date Issue: 2018
Appears in Collections:FEM - Tese e Dissertação

Files in This Item:
File SizeFormat 
BusatoJunior_Edgar_M.pdf8.26 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.