Title: Avaliação da adaptação e retenção de restaurações cerâmicas com diferentes alívios internos a pilares bases de titânio
Title Alternative: Evaluation of adaptation and retention of ceramic restorations with different internal gap to titanium bases
Author: Pacheco, Ney Diegues, 1976-
Advisor: Del Bel Cury, Altair Antoninha, 1948-
Abstract: Resumo: Frente à crescente demanda por procedimentos estéticos, a utilização de cerâmicas de alta resistência está cada vez mais comum na implantodontia. A utilização de pilares em cerâmica pura vem apresentando comportamento mecânico e interação desfavorável com as superfícies de conexão com os implantes. Como alternativa, restaurações cerâmicas com coloração e perfil de emergência personalizados podem ser confeccionadas através de sistemas CAD/CAM e cimentadas sobre bases de titânio fora da cavidade oral, permitindo controle sobre escoamento de cimento e acabamento das margens. Diversos sistemas digitais que empregam tecnologia CAD/CAM comercialmente disponíveis podem ser utilizados para confecção de restaurações sobre bases de titânio, otimizando o processo de fabricação e podendo apresentar superioridade quanto à adaptação marginal e interna, quando comparados aos sistemas convencionais. Diferentes fabricantes disponibilizam bibliotecas digitais de seus produtos, onde padrões de alívio interno são pré-determinados. Não há consenso de qual padrão de alívio interno proporciona melhor comportamento mecânico e nem qual a influência deste na adaptação interna e marginal de próteses cerâmicas. No presente estudo, foram cimentadas adesivamente, com Panavia F (Kuraray), trinta e seis estruturas (n=36) em zircônia Ceramill ZOLID FX (Amann Girrbach) com 3 diferentes espaçamentos internos (25 µm, 50 µm e 75 µm) sobre bases de titânio (Link ¿ Neodent), sendo 12 estruturas por grupo. Em seguida, foram obtidas medidas da adaptação marginal e interna através de microscopia ótica, e submetidas a arrancamento (Pull out) em máquina universal de ensaios com velocidade de 0.5 mm/min., então analisadas comparativamente. Resultados foram comparados estatisticamente através de teste Tukey com nível de significância de 5% e correlação de Pearson. Não houve correlação entre os diferentes desajustes internos e a resistência ao arrancamento (p>0,05) e nem influência significativa dos diferentes espaçamentos internos na adaptação marginal (p>0,05). Somente foi observada diferença estatisticamente significativa (p<0,05) nas medidas de desajuste interno na região cervical. Todos os grupos testados apresentaram desajustes marginais verticais dentro dos limites clinicamente aceitáveis (120 µm). Os diferentes desajustes internos testados não influenciaram nos valores de resistência ao arrancamento

Abstract: Due to the increasing demand for aesthetic procedures, the use of high-strength ceramics is coming every day more common in implantology. The use of ceramic abutments has presented poor mechanical behavior and unfavorable interaction with the implant connections. As an alternative, ceramic restorations with custom staining and emergency profile can be made using CAD/CAM systems and chairside cemented on titanium bases out of the mouth, allowing control over cement excess flow and margins finishing. Many commercially available digital systems using CAD/CAM technology could be used to produce restorations over titanium bases, optimizing the fabrication process and maybe showing better marginal and internal adaptation when compared to conventional systems. Different manufacturers offer digital library of their products where pre-defined internal gaps are available. There is no consensus regarding which internal gap offer better mechanical behavior as well as what is this influence on internal and marginal ceramic prosthesis adaptation. In the present study, thirty - six coppings (n = 36) of Ceramill ZOLID FX zirconia (Amann Girrbach) with three different internal gaps (25 µm, 50 µm e 75 µm) were cemented with Panavia F (Kuraray) on titanium bases (Link - Neodent), 12 on each group. Then, measurements of the marginal and internal interfaces were obtained by optical microscopy, and subjected to pull out in a universal machine with 0.5 mm / min head velocity, then analyzed comparatively. Results were compared statistically by Tukey test with significance level of 5% and Pearson's correlation. There was no correlation between the different internal gaps and Pull out resistance (p> 0.05) and no significant influence of the different internal gaps in the marginal adaptation (p> 0.05). Only a statistically significant difference (p <0.05) was observed in measures of internal gaps in the cervical region. All groups tested showed vertical marginal discrepancy within the clinically acceptable limits (120 µm). There was no influence of tested internal gap levels on pull out resistance
Subject: Projeto auxiliado por computador
Implantes dentários
Microscopia
Adaptação marginal dentária
Óxido de zircônio
Language: Português
Editor: [s.n.]
Citation: PACHECO, Ney Diegues. Avaliação da adaptação e retenção de restaurações cerâmicas com diferentes alívios internos a pilares bases de titânio. 2018. 1 recurso online (71 p.). Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP.
Date Issue: 2018
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Pacheco_NeyDiegues_D.pdf660.52 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.