Please use this identifier to cite or link to this item: http://repositorio.unicamp.br/jspui/handle/REPOSIP/332176
Type: TESE DIGITAL
Degree Level: Doutorado
Title: Influência do protocolo adesivo nas propriedades físico-químicas e resistência de união à cerâmica de cimentos resinosos experimentais contendo sistema fotoiniciador ternário : Influence of adhesive protocol on physicochemical properties and ceramic bond strength of experimental resin cements containing ternary photoinitiator system
Title Alternative: Influence of adhesive protocol on physicochemical properties and ceramic bond strength of experimental resin cements containing ternary photoinitiator system
Author: Palialol, Alan Rodrigo Muniz, 1984-
Advisor: Marchi, Giselle Maria, 1970-
Abstract: Resumo: No presente estudo foi avaliado a influência do protocolo adesivo nas propriedades físico-químicas e resistência de união (RU) à cerâmica de cimentos resinosos experimentais (CREs) contendo um sistema fotoiniciador ternário. Foram preparados cinco formulações de CREs contendo como base os monômeros Bis-GMA e TEGDMA (na proporção 1:1 em massa). O sistema fotoiniciador foi composto por 1 mol% de canforoquinona, 2 mol% de amina terciária 2-(dimetilamino) etil metacrilato e diferentes concentrações do sal hexafluorofosfato de difeniliodôno (DFI): 0(controle); 0,25; 0,5; 1 e 2 mol%, definindo assim, cinco formulações de CREs. Como inibidor, foi acrescido à mistura 0,1 mol% de hidroxitolueno butilado e 60% em peso de partículas silanizadas de vidro de bário-alumínio-silicato foram incorporadas como carga inorgânica. Diante disso, dez grupos foram estabelecidos de modo que metade foi confeccionado sem a mistura com adesivo Adper Scotchbond Multi-Purpose - bond (G1 ¿ G5) e a outra metade com a mistura de 3 ?l de adesivo (G6 - G10). A fotoativação, para todos os testes, foi realizada através de um bloco de cerâmica IPS e.max com LED Bluephase G2 a 1265.6 mW/cm2 por 60 segundos. Para o teste de RU foram confeccionados setenta espécimes (n=7) de cerâmica IPS e.max (10 mm x 10 mm x 3 mm). Os espécimes foram cimentados em blocos de resina fotopolimerizável Filtek Z250 (10 mm x 10 mm x 5 mm). Após armazenamento em estufa por 24 horas a 37oC, as amostras foram seccionadas para obtenção de palitos (25 a 30 por bloco). Metade dos palitos de cada bloco foram submetidos ao ensaio de microtração imediato em máquina de ensaio universal EMIC (velocidade de 0,5 mm/min). A outra metade foi separada para o teste de microtração após armazenamento em água destilada pelo período de um ano. Foi realizado análise do padrão de fratura em lupa estereoscópica (Leica MZ75). Adicionalmente, foi avaliado a resistência coesiva (RC) dos CREs (n=10), cinética de polimerização e grau de conversão (GC) em espectrômetro de infravermelho transformado de Fourier (FTIR) (n=5) e teste de sorção e solubilidade (SS) (n=5). Os dados foram analisados através do teste de análise de variância (medidas repetidas para RU e 2 fatores para os demais testes) e teste Tukey, a um nível de significância de 5%. Para os valores de RU, não houve diferença estatísitca entre os grupos, tanto no tempo imediato quanto após o armazenamento (p0,05). Da mesma forma, não houve diferença estatística entre os tempos imediato e após armazenamento (p0,05). O grupo 0 mol% DFI apresentou os maiores valores de solubilidade e os menores valores para GC e RC (p0,05). Os demais grupos apresentaram valores semelhantes entre si (p0,05). A adição do adesivo aumentou os valores de GC apenas para o grupo 0 mol% DFI (p0,05). A adição do sal DFI melhorou a reatividade e as propriedades físico-químicas dos CREs, porém, não foi capaz de aumentar a RU à cerâmica. O uso do adesivo não exerceu influência nas propriedades físico-químicas dos CREs contendo sal de DFI. O armazenamento em água destilada por um ano não reduziu a RU à cerâmica

Abstract: The present study evaluated the influence of an adhesive protocol on physicochemical properties and ceramic bond strength (BS) of experimental resin cements (ERCs) containing a ternary photoinitiator system. For this purpose, five ERCs were prepared using a Bis-GMA/TEGDMA (1:1 molar ratio) base compound. The photoinitiator system was composed by 1 mol% of camphorquinone, 2 mol% of dimethylaminoethil methacrylate and different diphenyliodonium hexafluorophosphate (DPI) salt different concentrations of 0, 0.25, 0.5, 1 or 2 mol%, resulting in five ERCs. As an inhibitor, 0.1mol% of hydroxyl butyl toluene was used and a 60% in weigth of silanated barium-aluminum-silicate glass for fillers particles. Thus, ten groups were established so that one half was performed without adhesive mixture (G1-G5) and the other half (G6-G10) with adhesive mixture of 3 ?l of Adper Scotchbond Multi-Purpose ¿ Bond. For all laboratory tests, the light curing was performed through an IPS e.max ceramic block with Bluephase G2 light source at 1265.5 mW/cm2 for 60 seconds. Seventy IPS e.max Press ceramic specimens (10 mm x 10 mm x 3 mm) were fabricated and randomly divided among the ten groups previously established. The specimens were fixed to light curing composite resin Filtek Z250 blocks (10 mm x 10 mm x 5 mm). After storage for 24 hours at 37oC, the specimens were sectioned perpendicular to the bond interface (25 to 30 beams per block) and half of the beams of each block were submitted to immediate microtensile bond strength test. The other half was separated for the microtensile test after storage in distilled water for one year. The failure mode was analyzed by a stereomicroscope (Leica MZ75) at 40x magnification. Additionally, it was evaluated the ultimate tensile strength (UTS) of ERCs using hourglass shape specimens (n=10). Degree of conversion (DC) and real-time polymerization kinetics were measured in disc shape specimens (n=5) using near-infrared spectroscopy (NIRS). Water up take and solubility (WS) were assessed too using disc shape specimens (n=5). Data were analyzed using analysis of variance (repeated measures for BS test and two criteria for the other tests) and Tukey test at a significance level of 5%. For immediate and after water storage BS values, there was no statistical difference between groups (p0,05). Similarly, there was no statistical difference between immediate and after one year of water storage (p0,05). The 0 mol% DPI ERC showed the higher values of WS and the lower values for DC, maximum rate of polymerization and UTS (p0,05). The others ERCs presented similar values and were not statistically different from each other (p0,05). The addition of adhesive led to higher DC values only for 0 mol% DPI ERC (p0,05). The addition of DPI salt improve the reactivity and physicochemical properties of ERCs. The adhesive had no influence on the physicochemical properties of ERCs containing DPI salt. Addition of a DPI salt to light-activated ERCs increased its DC, but was not able to increase the BS between the ceramic and resin materials. For this study, one year of water storage was not capable of jeopardizing ceramic BS
Subject: Cerâmica
Cimentos de resina
Adesivos
Fotopolimerização
Language: Multilíngua
Editor: [s.n.]
Citation: PALIALOL, Alan Rodrigo Muniz. Influência do protocolo adesivo nas propriedades físico-químicas e resistência de união à cerâmica de cimentos resinosos experimentais contendo sistema fotoiniciador ternário: Influence of adhesive protocol on physicochemical properties and ceramic bond strength of experimental resin cements containing ternary photoinitiator system. 2017. 1 recurso online (52 p.). Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP.
Date Issue: 2017
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Palialol_AlanRodrigoMuniz_D.pdf7.59 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.