Title: Resistência da união de materiais restauradores CAD/CAM tratados com diferentes protocolos de condicionamento de superfície = Bond strength of CAD/CAM restorative materials treated with different surface etching protocols
Title Alternative: Bond strength of CAD/CAM restorative materials treated with different surface etching protocols
Author: Colombo, Lucas do Amaral, 1993-
Advisor: Goes, Mario Fernando de, 1954-
Abstract: Resumo: O objetivo neste estudo foi avaliar diferentes protocolos de tratamento de superfície de materiais cerâmicos CAD/CAM em relação à morfologia e resistência da união entre cerâmica e cimento resinoso. Foram elaborados protocolos de tratamento de superfície(n=10) baseados nas recomendações do fabricante, variando a concentração e o tempo de aplicação do ácido fluorídrico seguido pela aplicação de silano(HF5%20s+S, HF5%60s+S, HF10%20s+S, HF10%60s+S), assim como o uso um primer cerâmico autocondicionante(MBEP), além de um grupo controle(CT). Estes tratamentos foram executados em três materiais: cerâmica à base de dissilicato de lítio(IPS e.max CAD), à base de leucita(IPS Empress CAD) e cerâmica infiltrada por polímero(ENAMIC). As cerâmicas foram fixadas com cimento resinoso a um bloco de resina composta preparada para CAD/CAM e seccionadas em uma cortadeira de precisão, sob irrigação constante, até a obtenção de espécimes em forma de palitos. Todos os espécimes foram submetidos ao ensaio de microtração, sob velocidade de 0,5mm/min. A análise morfológica da superfície cerâmica tratada e o modo de fratura foram avaliados com microscópio eletrônico de varredura. Todos os dados foram submetidos à análise de variância à dois fatores e ao teste de Tukey (?=0.05). Os resultados mostraram que todos os tratamentos aumentaram significativamente a resistência da união em comparação com o grupo controle. Entretanto, as variações da concentração e do tempo de aplicação do ácido fluorídrico não influenciaram significativamente a resistência da união em nenhum dos materiais avaliados, inclusive não sendo estatisticamente diferentes do grupo tratado com primer cerâmico autocondicionante. A cerâmica infiltrada por polímero foi o material que apresentou valores médios significativamente maiores de resistência da união, enquanto as ceramicas à base de dissilicato de lítio e à base de leucita não apresentaram diferenças estatisticamente significativas entre si. O padrão de fratura mais prevalente em todos os grupos foi falha mista, seguido por falha coesiva no cimento resinoso. A morfologia da superfície da cerâmica apresentou alterações mais evidentes nos grupos de maior concentração e maior tempo de aplicação do ácido fluorídrico. O grupo tratado com o primer cerâmico autocondicionante mostrou alterações mais suaves nas superfícies cerâmicas. Assim, observou-se que todos os tratamentos contribuíram para melhorar a adesão das superfícies cerâmicas ao cimento resinoso. Enquanto a variação da concentração e do tempo de aplicação do ácido fluorídrico não influenciaram nos valores de resistência da união, o primer cerâmico autocondicionante apresentou menor alteração morfológica e mostrou-se tão eficiente quanto os tratamentos convencionais à base de ácido fluorídrico mais silano

Abstract: The objective of this study was to evaluate different protocols for surface treatment of CAD/ CAM ceramic materials on the surface morphology and bond strength between ceramic and resin cement. Surface treatment protocols were elaborate based on the manufacturer's instructions, varying the concentration and application time of hydrofluoric acid followed by application of silane(HF5%20s+S, HF5%60s+S, HF10%20s+S, HF10%60s+S), as well as the use of a self-etching ceramic primer(MBEP) and a control group(CT). The same surface treatments were performed on three ceramic materials: lithium disilicate based ceramics(IPS e.max CAD), leucite based ceramics(IPS Empress CAD), and polymer infiltrated ceramics(ENAMIC). The materials were cemented with a resin cement to a block of nanoceramic resin and sectioned using a precision cutter at a speed of 300 rpm and constant water irrigation to obtain stick shaped specimens, which were subjected to microtensile test. The morphological analysis of the fracture was evaluated with a scanning electron microscope. All data were submitted to two-way analysis of variance and Tukey's test (? = 0.05). The results showed that all experimental treatments improved bond strength when compared to the control group, however the variation of the concentration and application time of hydrofluoric acid did not influence the bond strength on any of the materials tested, being statistically equal to the group treated with self-etching primer. The polymer infiltrated ceramic was the material that presented higher values of bond strength, and the lithium disilicate and leucite base ceramics showed no statistically significant differences between each other. The most prevalent failure mode in all groups was mixed failure followed by cohesive on the resin cement. The surface morphology analysis was evaluated with a scanning electron microscope. The most evident surface changes were observed in the groups in which the concentration and application time of hydrofluoric acid were higher. The less evident change was noticed on the groups treated with self-etching primer. In conclusion, it was observed that all of the surface treatments tested improved the adhesion of the ceramics to the resin cement, but no differences were observed in this improvement with the variation of the concentration and the time of application of the hydrofluoric acid. In addition, the self-etching ceramic primer proved to be as efficient as conventional hydrofluoric acid plus silane treatments
Subject: Cerâmica odontológica
Projeto auxiliado por computador
Acido fluoridrico
Language: Multilíngua
Editor: [s.n.]
Citation: COLOMBO, Lucas do Amaral. Resistência da união de materiais restauradores CAD/CAM tratados com diferentes protocolos de condicionamento de superfície = Bond strength of CAD/CAM restorative materials treated with different surface etching protocols. 2018. 1 recurso online (47 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/331646>. Acesso em: 3 set. 2018.
Date Issue: 2018
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Colombo_LucasDoAmaral_M.pdf1.8 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.