Title: Caracterização de tensões residuais em diferentes cerâmicas de cobertura para prótese total fixa com infraestrutura de zircônia = Characterization of residual stresses in different veneering ceramics for full-arch fixed prosthese with zirconia framework
Title Alternative: Characterization of residual stresses in different veneering ceramics for full-arch fixed prosthese with zirconia framework
Author: Reginato, Vagner Flávio, 1993-
Advisor: Consani, Rafael Leonardo Xediek, 1974-
Abstract: Resumo: A fratura, trinca ou delaminação da cerâmica de cobertura sobre as infraestruturas de zircônia estão entre as principais falhas deste tipo de restauração. Um fator apontado como responsável por essas fraturas é a tensão resultante do processo de sinterização das cerâmicas. O objetivo neste estudo foi avaliar a influência do coeficiente de expansão térmica (CET) e da temperatura de transição vítrea (Tg) de três cerâmicas feldspática utilizadas para o recobrimento de infraestrutura de zircônia em prótese total fixa. A tensão residual e contração linear após a simulação do processo de esfriamento e carga oclusal foram mensuradas. A análise foi efetuada pelo método por elementos finitos num modelo tridimensional de uma prótese total maxilar com infraestrutura em zircônia (e.max ZirCAD) recoberta por três cerâmica felsdpática (Vita VM9, IPS e.max Ceram ou Lava Ceram). A simulação da contração linear foi realizada pelo esfriamento da estrutura a partir da Tg de cada cerâmica de cobertura até a temperatura ambiente (25?C). As cerâmicas de cobertura usadas tiveram valores de CTE de 5, 10 e 15% inferior à zircônia. Em seguida, um carregamento de 100 N na região oclusal de primeiro molar foi realizado. A magnitude da tensão máxima principal e contração linear foram avaliados. Os níveis de diferença de CTE entre cerâmica de cobertura e infraestrutura não apresentaram influência significante na tensão máxima principal e na contração linear. Os valores da Tg da cerâmica de cobertura mostraram ser diretamente proporcionais à quantidade de tensão máxima principal e contração linear. O GEC apresentou os maiores valores de tensão máxima principal e contração linear, enquanto os grupos GVM e GLC não apresentaram diferença significante entre si. Níveis de CTE da cerâmica de cobertura entre 5 e 15% menores que a infraestrutura não apresentaram influência significante nas tensões residuais e contração linear. A Tg apresentou efeito significante na tensão máxima principal e contração linear

Abstract: Fracture, crack or delamination of the veneering ceramic on the zirconia framework are some of the major flaws of this type of restoration. A factor identified as responsible for these fractures is the stress derived from the sintering process of ceramics. The aim of this study was to evaluate the influence of the coefficient of thermal expansion (CTE or ?) and glass transition temperature (Tg) of three veneering ceramics used for zirconia frameworks of full-arch fixed prostheses. The generation of residual stresses and linear contraction after the simulation of the cooling process and mechanical loading were measured. The analysis was based on the finite element method in three-dimensional model of a maxillary full-arch fixed prosthesis with zirconia framework (e.max ZirCAD) veneer by felsdpathic ceramics (Vita VM9, IPS e.max Ceram or Lava Ceram). The linear contraction simulation was performed by cooling the structures from the Tg of each veneer ceramic at room temperature (25°C). The veneering ceramics used showed CTEs of 5, 10 and 15% lower than the zirconia. A loading of 100 N on the occlusal region of the first molar was performed. The magnitude of the maximum principal stress and linear contraction were evaluated. The levels of CTE mismatch between veneering ceramics and framework showed no relevant influence on maximum principal stress and linear contraction. The Tg values of the veneer ceramic showed to be directly proportional to amount of maximum principal stress and linear contraction. The GEC presented the highest values of maximum principal stress and linear contraction. The GVM and GLC did not present significant differences between them. The CTE levels of veneering ceramics between 5 and 15% lower than framework did not show a relevant influence on residual stresses and linear contraction. The Tg showed a significant effect on ? max and linear contraction
Subject: Análise de elementos finitos
Implantes dentários
Prótese dentária completa
Zircônia tetragonal estabilizada por ítrio
Editor: [s.n.]
Citation: REGINATO, Vagner Flávio. Caracterização de tensões residuais em diferentes cerâmicas de cobertura para prótese total fixa com infraestrutura de zircônia = Characterization of residual stresses in different veneering ceramics for full-arch fixed prosthese with zirconia framework. 2017. 1 recurso online ( 39 p.). Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: <http://www.repositorio.unicamp.br/handle/REPOSIP/331394>. Acesso em: 1 set. 2018.
Date Issue: 2017
Appears in Collections:FOP - Tese e Dissertação

Files in This Item:
File SizeFormat 
Reginato_VagnerFlavio_M.pdf1.62 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.